Surface Morphology and Structural Evolution of Magnetite-Based Iron Ore Fines During the Oxidation

Publikationen: Beitrag in FachzeitschriftArtikelForschung(peer-reviewed)

Externe Organisationseinheiten

  • K1-MET GmbH, Linz
  • University of Science and Technology Beijing
  • Primetals Technologies Austria GmbH
  • Wuhan University of Science and Technology
  • South Ural State University

Abstract

The use of magnetite-based iron ore fines by means of fluidized bed technology has become a promising route to produce direct reduced iron. The significant influence of a prior oxidation treatment, which occurs in the preheating stage, on the subsequent fluidization and reduction behavior was observed in our previous study. As a result, it is important to investigate the oxidation of magnetite-based iron ore fines for an optimization of the proposed route. Three magnetite-based iron ore brands were analyzed. The oxidation characteristics are investigated based on thermogravimetric analysis. The surface morphology, structural evolution, and phase transformation were studied with a scanning electron microscope, an optical light microscope, and a high-temperature-X-ray diffraction (HT-XRD), respectively. The three samples showed different oxidation capacity indexes (OCIs) but similar TG-DTG curves. The oxidation rate peaks at around 330 °C and 550 °C indicated the formation of γ-Fe2O3 and α-Fe2O3. The hematite phase shows a particular growth habit. The oxidation first occurs at the surface, forming gridlike hematite structures, and then extends to the inside, resulting in hematite needles. The specific surface area and pore volume decrease significantly due to the sintering effect during oxidation.

Details

OriginalspracheEnglisch
Seiten (von - bis)1644-1660
Seitenumfang17
FachzeitschriftMetallurgical and materials transactions. B, Process metallurgy and materials processing science
Jahrgang53.2022
Ausgabenummer3
DOIs
StatusElektronische Veröffentlichung vor Drucklegung. - 23 März 2022