Identification and Analysis of Potential Retarders for Geopolymers Designed for Well Cementing

Publikationen: Thesis / Studienabschlussarbeiten und HabilitationsschriftenMasterarbeit

Standard

Identification and Analysis of Potential Retarders for Geopolymers Designed for Well Cementing. / Eid, Elsayed Adel Ahmed Ibrahim.
2020.

Publikationen: Thesis / Studienabschlussarbeiten und HabilitationsschriftenMasterarbeit

Bibtex - Download

@mastersthesis{c00af9233b2243cf8c5143fe6c00789d,
title = "Identification and Analysis of Potential Retarders for Geopolymers Designed for Well Cementing",
abstract = "Ordinary Portland cement (OPC) is the primary material, which is used in oil well cement, isolation formation and plug and abandonment. OPC has many advantages and some limitations reviewed by different authors. The limitations associated with cement cause well integrity issues, risking humans, and environment. Several studies and experiments are conducted to evaluate different materials, which could be an optimal alternate to OPC. Geopolymer is one of these materials, which has been tested in lab scale to find its potential to replace OPC. Geopolymers are inorganic materials based on rock sources, which are rich in aluminum silicates. Many pieces of research have conducted on the geopolymer to assess its characteristics and properties. Studies showed that geopolymer is a ductile and low shrinkage material. It develops sufficient bond strength, high compressive strength and less fluid loss comparing to OPC. However, studies showed some shortcomings of geopolymer, which should be enhanced to allow using the geopolymer in the oil field. The pumpability at elevated temperatures, for a certain period, is one of the current limitations of the geopolymer. Several experiments have been performed to get the proper compositions of the geopolymer and the appropriate retarding admixture, which help to increase the pumping time of the geopolymer paste. Chemical S&H revealed its potential to retard the setting time by 80 mins. It is proved that there many parameters, which control the setting time of the sample. The modular ratio, weight of the admixture and composition of the precursors, have an impact on delaying the thickening time. BS2 is more pumpability than BS1, and S7 is the sample which has the most significant pumping time among the others. Results from the uniaxial compressive test (UCS) and ultrasonic cement analyzer (UCA) show the compressive strength value is in an acceptable range for utilization in oil well cementing. Rheology properties of geopolymers were characterized as non-Newtonian shear-thinning fluid and its density within the permissible range (1.95 sg). These characteristics promote the geopolymer to be a good quality alternative material to be applied in downhole applications.",
keywords = "Geopolymer, Aktivator, Verz{\"o}gerer, Aluminiumsilikate, Inorganic polymers, Geopolymer, Activator, Retarders, Aluminum silicates, Inorganic polymers",
author = "Eid, {Elsayed Adel Ahmed Ibrahim}",
note = "embargoed until null",
year = "2020",
language = "English",
school = "Montanuniversitaet Leoben (000)",

}

RIS (suitable for import to EndNote) - Download

TY - THES

T1 - Identification and Analysis of Potential Retarders for Geopolymers Designed for Well Cementing

AU - Eid, Elsayed Adel Ahmed Ibrahim

N1 - embargoed until null

PY - 2020

Y1 - 2020

N2 - Ordinary Portland cement (OPC) is the primary material, which is used in oil well cement, isolation formation and plug and abandonment. OPC has many advantages and some limitations reviewed by different authors. The limitations associated with cement cause well integrity issues, risking humans, and environment. Several studies and experiments are conducted to evaluate different materials, which could be an optimal alternate to OPC. Geopolymer is one of these materials, which has been tested in lab scale to find its potential to replace OPC. Geopolymers are inorganic materials based on rock sources, which are rich in aluminum silicates. Many pieces of research have conducted on the geopolymer to assess its characteristics and properties. Studies showed that geopolymer is a ductile and low shrinkage material. It develops sufficient bond strength, high compressive strength and less fluid loss comparing to OPC. However, studies showed some shortcomings of geopolymer, which should be enhanced to allow using the geopolymer in the oil field. The pumpability at elevated temperatures, for a certain period, is one of the current limitations of the geopolymer. Several experiments have been performed to get the proper compositions of the geopolymer and the appropriate retarding admixture, which help to increase the pumping time of the geopolymer paste. Chemical S&H revealed its potential to retard the setting time by 80 mins. It is proved that there many parameters, which control the setting time of the sample. The modular ratio, weight of the admixture and composition of the precursors, have an impact on delaying the thickening time. BS2 is more pumpability than BS1, and S7 is the sample which has the most significant pumping time among the others. Results from the uniaxial compressive test (UCS) and ultrasonic cement analyzer (UCA) show the compressive strength value is in an acceptable range for utilization in oil well cementing. Rheology properties of geopolymers were characterized as non-Newtonian shear-thinning fluid and its density within the permissible range (1.95 sg). These characteristics promote the geopolymer to be a good quality alternative material to be applied in downhole applications.

AB - Ordinary Portland cement (OPC) is the primary material, which is used in oil well cement, isolation formation and plug and abandonment. OPC has many advantages and some limitations reviewed by different authors. The limitations associated with cement cause well integrity issues, risking humans, and environment. Several studies and experiments are conducted to evaluate different materials, which could be an optimal alternate to OPC. Geopolymer is one of these materials, which has been tested in lab scale to find its potential to replace OPC. Geopolymers are inorganic materials based on rock sources, which are rich in aluminum silicates. Many pieces of research have conducted on the geopolymer to assess its characteristics and properties. Studies showed that geopolymer is a ductile and low shrinkage material. It develops sufficient bond strength, high compressive strength and less fluid loss comparing to OPC. However, studies showed some shortcomings of geopolymer, which should be enhanced to allow using the geopolymer in the oil field. The pumpability at elevated temperatures, for a certain period, is one of the current limitations of the geopolymer. Several experiments have been performed to get the proper compositions of the geopolymer and the appropriate retarding admixture, which help to increase the pumping time of the geopolymer paste. Chemical S&H revealed its potential to retard the setting time by 80 mins. It is proved that there many parameters, which control the setting time of the sample. The modular ratio, weight of the admixture and composition of the precursors, have an impact on delaying the thickening time. BS2 is more pumpability than BS1, and S7 is the sample which has the most significant pumping time among the others. Results from the uniaxial compressive test (UCS) and ultrasonic cement analyzer (UCA) show the compressive strength value is in an acceptable range for utilization in oil well cementing. Rheology properties of geopolymers were characterized as non-Newtonian shear-thinning fluid and its density within the permissible range (1.95 sg). These characteristics promote the geopolymer to be a good quality alternative material to be applied in downhole applications.

KW - Geopolymer

KW - Aktivator

KW - Verzögerer

KW - Aluminiumsilikate

KW - Inorganic polymers

KW - Geopolymer

KW - Activator

KW - Retarders

KW - Aluminum silicates

KW - Inorganic polymers

M3 - Master's Thesis

ER -