Development and characterization of a new near-alpha-titanium alloy for high performance applications

Publikationen: Thesis / Studienabschlussarbeiten und HabilitationsschriftenDiplomarbeit

Standard

Development and characterization of a new near-alpha-titanium alloy for high performance applications. / Proprentner, Daniela.
2007.

Publikationen: Thesis / Studienabschlussarbeiten und HabilitationsschriftenDiplomarbeit

Bibtex - Download

@phdthesis{3961cfecd6e048fdb5fd631f2595a07d,
title = "Development and characterization of a new near-alpha-titanium alloy for high performance applications",
abstract = "Common near-alpha-titanium alloys are designed for high-temperature applications up to 600°C. These alloys combine excellent creep behavior with high specific strength at elevated temperatures. Therefore, these materials are used for applications in aerospace and automotive industry. Prior to this diploma thesis a new near-alpha-titanium alloy with an restricted intermetallic content of 50 vol.% was developed for application up to 800°C service temperature. The microstructure, with and without heat-treatments, was analyzed by means of light optical and scanning electron microscopy. Tensile tests were performed at room and elevated temperatures to quantify the increase of strength after different heat-treatments. The annealed microstructure was described by means of quantitative phase analysis of light optical images, x-ray diffraction, electron back scattering diffraction and additional transmission electron microscopy. The deformation behavior of the material has been determined by a deformation dilatometer with additional characterization of the deformed microstructure. Furthermore, static high temperature oxidation test in air atmosphere were performed and compared with different titanium alloys.",
keywords = "titanium alloys near-alpha titanium alloys microstructure deformation behavior high temperature strength oxidation behavior, Titan-Legierung near-alpha-Titanlegierungen Mikrostruktur Umformverhalten Warmfestigkeit Oxidationsverhalten",
author = "Daniela Proprentner",
note = "embargoed until null",
year = "2007",
language = "English",
type = "Diploma Thesis",

}

RIS (suitable for import to EndNote) - Download

TY - THES

T1 - Development and characterization of a new near-alpha-titanium alloy for high performance applications

AU - Proprentner, Daniela

N1 - embargoed until null

PY - 2007

Y1 - 2007

N2 - Common near-alpha-titanium alloys are designed for high-temperature applications up to 600°C. These alloys combine excellent creep behavior with high specific strength at elevated temperatures. Therefore, these materials are used for applications in aerospace and automotive industry. Prior to this diploma thesis a new near-alpha-titanium alloy with an restricted intermetallic content of 50 vol.% was developed for application up to 800°C service temperature. The microstructure, with and without heat-treatments, was analyzed by means of light optical and scanning electron microscopy. Tensile tests were performed at room and elevated temperatures to quantify the increase of strength after different heat-treatments. The annealed microstructure was described by means of quantitative phase analysis of light optical images, x-ray diffraction, electron back scattering diffraction and additional transmission electron microscopy. The deformation behavior of the material has been determined by a deformation dilatometer with additional characterization of the deformed microstructure. Furthermore, static high temperature oxidation test in air atmosphere were performed and compared with different titanium alloys.

AB - Common near-alpha-titanium alloys are designed for high-temperature applications up to 600°C. These alloys combine excellent creep behavior with high specific strength at elevated temperatures. Therefore, these materials are used for applications in aerospace and automotive industry. Prior to this diploma thesis a new near-alpha-titanium alloy with an restricted intermetallic content of 50 vol.% was developed for application up to 800°C service temperature. The microstructure, with and without heat-treatments, was analyzed by means of light optical and scanning electron microscopy. Tensile tests were performed at room and elevated temperatures to quantify the increase of strength after different heat-treatments. The annealed microstructure was described by means of quantitative phase analysis of light optical images, x-ray diffraction, electron back scattering diffraction and additional transmission electron microscopy. The deformation behavior of the material has been determined by a deformation dilatometer with additional characterization of the deformed microstructure. Furthermore, static high temperature oxidation test in air atmosphere were performed and compared with different titanium alloys.

KW - titanium alloys near-alpha titanium alloys microstructure deformation behavior high temperature strength oxidation behavior

KW - Titan-Legierung near-alpha-Titanlegierungen Mikrostruktur Umformverhalten Warmfestigkeit Oxidationsverhalten

M3 - Diploma Thesis

ER -