Annealing activated substrate element diffusion and its influence on the microstructure and mechanical properties of CVD TiN/TiCN coatings
Publikationen: Beitrag in Fachzeitschrift › Artikel › Forschung › (peer-reviewed)
Standard
in: Surface & coatings technology, Jahrgang 488.2024, Nr. 30 July, 131079, 2024.
Publikationen: Beitrag in Fachzeitschrift › Artikel › Forschung › (peer-reviewed)
Harvard
APA
Vancouver
Author
Bibtex - Download
}
RIS (suitable for import to EndNote) - Download
TY - JOUR
T1 - Annealing activated substrate element diffusion and its influence on the microstructure and mechanical properties of CVD TiN/TiCN coatings
AU - Konstantiniuk, Fabian
AU - Schiester, Maximilian
AU - Tkadletz, Michael
AU - Czettl, Christoph
AU - Schalk, Nina
PY - 2024
Y1 - 2024
N2 - TiN/TiCN deposited by chemical vapor deposition (CVD) is widely used as hard coating system for cemented carbide cutting tools, typically under an Al2O3 top layer. During the deposition of the Al2O3 top layer, the underlying TiN and TiCN layers are exposed to high temperatures. Therefore, the present study focuses on the influence of this Al2O3 deposition step, which is mimicked by a vacuum-annealing treatment, on the microstructure and mechanical properties of the TiN/TiCN coating. By applying advanced characterization techniques such as scanning electron microscopy, scanning transmission electron microscopy, transmission Kikuchi diffraction, atom probe tomography, and micro-mechanical bending tests on both, as-deposited and annealed coatings, changes in the microstructure and mechanical properties were studied. It was found that W and Co diffusion occurs along the TiN and TiCN grain boundaries from the substrate into the coating. While the hardness, Young's modulus, and fracture toughness remained unaffected by the annealing treatment, a significant decrease of the fracture stress with increasing annealing time was observed. The present study provides a fundamental understanding of substrate element diffusion in CVD TiN/TiCN coatings deposited on cemented carbide substrates.
AB - TiN/TiCN deposited by chemical vapor deposition (CVD) is widely used as hard coating system for cemented carbide cutting tools, typically under an Al2O3 top layer. During the deposition of the Al2O3 top layer, the underlying TiN and TiCN layers are exposed to high temperatures. Therefore, the present study focuses on the influence of this Al2O3 deposition step, which is mimicked by a vacuum-annealing treatment, on the microstructure and mechanical properties of the TiN/TiCN coating. By applying advanced characterization techniques such as scanning electron microscopy, scanning transmission electron microscopy, transmission Kikuchi diffraction, atom probe tomography, and micro-mechanical bending tests on both, as-deposited and annealed coatings, changes in the microstructure and mechanical properties were studied. It was found that W and Co diffusion occurs along the TiN and TiCN grain boundaries from the substrate into the coating. While the hardness, Young's modulus, and fracture toughness remained unaffected by the annealing treatment, a significant decrease of the fracture stress with increasing annealing time was observed. The present study provides a fundamental understanding of substrate element diffusion in CVD TiN/TiCN coatings deposited on cemented carbide substrates.
U2 - 10.1016/j.surfcoat.2024.131079
DO - 10.1016/j.surfcoat.2024.131079
M3 - Article
VL - 488.2024
JO - Surface & coatings technology
JF - Surface & coatings technology
SN - 0257-8972
IS - 30 July
M1 - 131079
ER -