Thermodynamic modeling of the Fe-Sn system including an experimental re-assessment of the liquid miscibility gap

Research output: Contribution to journalArticleResearchpeer-review

Standard

Thermodynamic modeling of the Fe-Sn system including an experimental re-assessment of the liquid miscibility gap. / Park, Won-Bum; Bernhard, Michael Christian; Presoly, Peter et al.
In: Journal of Materials Informatics, Vol. 3.2023, No. 5, 23.03.2023.

Research output: Contribution to journalArticleResearchpeer-review

Bibtex - Download

@article{cc1e940cf4034cd286014ea0d5ee0922,
title = "Thermodynamic modeling of the Fe-Sn system including an experimental re-assessment of the liquid miscibility gap",
abstract = "The usage of low-grade ferrous scrap has increased over decades to decrease CO2 emissions and to produce steel products at a low cost. A serious problem in melting post-consumer scrap material is the accumulation of tramp elements, e.g., Cu and Sn, in the liquid steel. These tramp elements are difficult to remove during conventional steelmaking processes. Sn is considered as one of the most harmful tramp elements because, together with Cu, it sometimes induces the liquid metal embrittlement in high-temperature ferrous processing, e.g., continuous casting and hot rolling. Furthermore, the chemical interaction between Fe and Sn plays an important role in the Sn smelting process. The raw material used in the Sn smelting process is SnO2 (cassiterite), in which Fe3O4 is a gangue in the Sn ore. In the process, the reduction of Fe3O4 is unavoidable, which results in forming a Fe-Sn alloy (hardhead). The recirculation of the hardhead decreases the furnace capacity and increases the energy consumption in the smelting. The need to efficiently recover Sn from secondary resources is therefore inevitable. The CALculation of PHAse Diagrams (CALPHAD) approach helps to predict the equilibrium state of the multicomponent system. Previously reported studies of the Fe-Sn system show inconsistencies in the calculations and the experimental results. Mainly the miscibility gap in the liquid phase was under debate, as experimental data of the phase boundary are scattered. Experimental study and re-optimization of model parameters were carried out with emphasis on the correct shape of the miscibility gap. Three different experimental techniques were employed: differential scanning calorimetry, electromagnetic levitation, and contact angle measurement. The present thermodynamic model has higher accuracy in predicting the solubility of Sn in the body-centered cubic (bcc), compared to previous assessments. This is achieved by re-evaluating the Gibbs energies of the FeSn and FeSn2 compounds and the peritectic reaction related to Fe5Sn3. Also, the inconsistencies related to the miscibility gap around XSn = 0.31-0.81 were resolved. The database developed in the present study can contribute to the development of a large CALPHAD database containing tramp elements.",
author = "Won-Bum Park and Bernhard, {Michael Christian} and Peter Presoly and Youn-Bae Kang",
year = "2023",
month = mar,
day = "23",
doi = "10.20517/jmi.2022.37",
language = "English",
volume = "3.2023",
journal = "Journal of Materials Informatics",
issn = "2770-372X",
number = "5",

}

RIS (suitable for import to EndNote) - Download

TY - JOUR

T1 - Thermodynamic modeling of the Fe-Sn system including an experimental re-assessment of the liquid miscibility gap

AU - Park, Won-Bum

AU - Bernhard, Michael Christian

AU - Presoly, Peter

AU - Kang, Youn-Bae

PY - 2023/3/23

Y1 - 2023/3/23

N2 - The usage of low-grade ferrous scrap has increased over decades to decrease CO2 emissions and to produce steel products at a low cost. A serious problem in melting post-consumer scrap material is the accumulation of tramp elements, e.g., Cu and Sn, in the liquid steel. These tramp elements are difficult to remove during conventional steelmaking processes. Sn is considered as one of the most harmful tramp elements because, together with Cu, it sometimes induces the liquid metal embrittlement in high-temperature ferrous processing, e.g., continuous casting and hot rolling. Furthermore, the chemical interaction between Fe and Sn plays an important role in the Sn smelting process. The raw material used in the Sn smelting process is SnO2 (cassiterite), in which Fe3O4 is a gangue in the Sn ore. In the process, the reduction of Fe3O4 is unavoidable, which results in forming a Fe-Sn alloy (hardhead). The recirculation of the hardhead decreases the furnace capacity and increases the energy consumption in the smelting. The need to efficiently recover Sn from secondary resources is therefore inevitable. The CALculation of PHAse Diagrams (CALPHAD) approach helps to predict the equilibrium state of the multicomponent system. Previously reported studies of the Fe-Sn system show inconsistencies in the calculations and the experimental results. Mainly the miscibility gap in the liquid phase was under debate, as experimental data of the phase boundary are scattered. Experimental study and re-optimization of model parameters were carried out with emphasis on the correct shape of the miscibility gap. Three different experimental techniques were employed: differential scanning calorimetry, electromagnetic levitation, and contact angle measurement. The present thermodynamic model has higher accuracy in predicting the solubility of Sn in the body-centered cubic (bcc), compared to previous assessments. This is achieved by re-evaluating the Gibbs energies of the FeSn and FeSn2 compounds and the peritectic reaction related to Fe5Sn3. Also, the inconsistencies related to the miscibility gap around XSn = 0.31-0.81 were resolved. The database developed in the present study can contribute to the development of a large CALPHAD database containing tramp elements.

AB - The usage of low-grade ferrous scrap has increased over decades to decrease CO2 emissions and to produce steel products at a low cost. A serious problem in melting post-consumer scrap material is the accumulation of tramp elements, e.g., Cu and Sn, in the liquid steel. These tramp elements are difficult to remove during conventional steelmaking processes. Sn is considered as one of the most harmful tramp elements because, together with Cu, it sometimes induces the liquid metal embrittlement in high-temperature ferrous processing, e.g., continuous casting and hot rolling. Furthermore, the chemical interaction between Fe and Sn plays an important role in the Sn smelting process. The raw material used in the Sn smelting process is SnO2 (cassiterite), in which Fe3O4 is a gangue in the Sn ore. In the process, the reduction of Fe3O4 is unavoidable, which results in forming a Fe-Sn alloy (hardhead). The recirculation of the hardhead decreases the furnace capacity and increases the energy consumption in the smelting. The need to efficiently recover Sn from secondary resources is therefore inevitable. The CALculation of PHAse Diagrams (CALPHAD) approach helps to predict the equilibrium state of the multicomponent system. Previously reported studies of the Fe-Sn system show inconsistencies in the calculations and the experimental results. Mainly the miscibility gap in the liquid phase was under debate, as experimental data of the phase boundary are scattered. Experimental study and re-optimization of model parameters were carried out with emphasis on the correct shape of the miscibility gap. Three different experimental techniques were employed: differential scanning calorimetry, electromagnetic levitation, and contact angle measurement. The present thermodynamic model has higher accuracy in predicting the solubility of Sn in the body-centered cubic (bcc), compared to previous assessments. This is achieved by re-evaluating the Gibbs energies of the FeSn and FeSn2 compounds and the peritectic reaction related to Fe5Sn3. Also, the inconsistencies related to the miscibility gap around XSn = 0.31-0.81 were resolved. The database developed in the present study can contribute to the development of a large CALPHAD database containing tramp elements.

U2 - 10.20517/jmi.2022.37

DO - 10.20517/jmi.2022.37

M3 - Article

VL - 3.2023

JO - Journal of Materials Informatics

JF - Journal of Materials Informatics

SN - 2770-372X

IS - 5

ER -