The role of Cu, Sn, and Ni on surface crack formation in continuous casting

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Standard

The role of Cu, Sn, and Ni on surface crack formation in continuous casting. / Gaiser, Georg; Bernhard, Christian; Winkler, Johann et al.
Proceedings of the 11th European Continuous Casting Conference 2024, Essen, Germany.. 2024.

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Harvard

Gaiser, G, Bernhard, C, Winkler, J, Lex, C, Ilie, S, Hahn, S & Burzic, D 2024, The role of Cu, Sn, and Ni on surface crack formation in continuous casting. in Proceedings of the 11th European Continuous Casting Conference 2024, Essen, Germany.. 10th European Continuous Casting Conference 2024, Essen, Germany, 7/10/24.

APA

Gaiser, G., Bernhard, C., Winkler, J., Lex, C., Ilie, S., Hahn, S., & Burzic, D. (2024). The role of Cu, Sn, and Ni on surface crack formation in continuous casting. In Proceedings of the 11th European Continuous Casting Conference 2024, Essen, Germany.

Vancouver

Gaiser G, Bernhard C, Winkler J, Lex C, Ilie S, Hahn S et al. The role of Cu, Sn, and Ni on surface crack formation in continuous casting. In Proceedings of the 11th European Continuous Casting Conference 2024, Essen, Germany.. 2024

Author

Gaiser, Georg ; Bernhard, Christian ; Winkler, Johann et al. / The role of Cu, Sn, and Ni on surface crack formation in continuous casting. Proceedings of the 11th European Continuous Casting Conference 2024, Essen, Germany.. 2024.

Bibtex - Download

@inproceedings{5999bb7437844e8f8b5519b78a7617db,
title = "The role of Cu, Sn, and Ni on surface crack formation in continuous casting",
abstract = "The decarbonization of steel production processes will lead to the increased use of scrap - including low-grade scrap - in the future. In addition to the more difficult control of some residuals in electric arc furnace steelmaking, tramp elements could also lead to problems in the manufacturing processes. In continuous casting, tramp elements such as Cu and Sn may cause network cracking and the so-called Cueq is still the most common indicator for surface defect susceptibility. This study addresses the experimental simulation of surface defect formation and the role of Cu, Sn, and Ni for the temperatures 900 and 1100 °C. Its goal is to define an optimized operational window for continuous casting. Experiments were conducted utilizing the in-situ material characterization by bending (IMC-B) test which characterizes the crack sensitivity of steel after controlled solidification and subsequent cooling under an adjustable water vapor atmosphere. The tests were performed on medium carbon steel with varying but moderate concentrations of Cu, Sn, and Ni. Results indicate that the simultaneous presence of Cu and Sn leads to a notable increase in the occurrence of surface cracks. This is attributable to the formation of partially liquid phases in the area of the grain boundaries due to selective oxidation. However, the introduction of Ni into the alloy composition demonstrates a substantial improvement in crack mitigation. This finding emphasizes the importance of carefully managed tramp element content, particularly Cu and Sn in the continuous casting process to minimize crack formation during straightening but also indicates a strong influence of thermal history and bending temperatures. ",
author = "Georg Gaiser and Christian Bernhard and Johann Winkler and Christoph Lex and Sergiu Ilie and Susanne Hahn and Denijel Burzic",
year = "2024",
month = oct,
day = "7",
language = "English",
booktitle = "Proceedings of the 11th European Continuous Casting Conference 2024, Essen, Germany.",
note = "10th European Continuous Casting Conference 2024 ; Conference date: 07-10-2024 Through 11-10-2024",

}

RIS (suitable for import to EndNote) - Download

TY - GEN

T1 - The role of Cu, Sn, and Ni on surface crack formation in continuous casting

AU - Gaiser, Georg

AU - Bernhard, Christian

AU - Winkler, Johann

AU - Lex, Christoph

AU - Ilie, Sergiu

AU - Hahn, Susanne

AU - Burzic, Denijel

PY - 2024/10/7

Y1 - 2024/10/7

N2 - The decarbonization of steel production processes will lead to the increased use of scrap - including low-grade scrap - in the future. In addition to the more difficult control of some residuals in electric arc furnace steelmaking, tramp elements could also lead to problems in the manufacturing processes. In continuous casting, tramp elements such as Cu and Sn may cause network cracking and the so-called Cueq is still the most common indicator for surface defect susceptibility. This study addresses the experimental simulation of surface defect formation and the role of Cu, Sn, and Ni for the temperatures 900 and 1100 °C. Its goal is to define an optimized operational window for continuous casting. Experiments were conducted utilizing the in-situ material characterization by bending (IMC-B) test which characterizes the crack sensitivity of steel after controlled solidification and subsequent cooling under an adjustable water vapor atmosphere. The tests were performed on medium carbon steel with varying but moderate concentrations of Cu, Sn, and Ni. Results indicate that the simultaneous presence of Cu and Sn leads to a notable increase in the occurrence of surface cracks. This is attributable to the formation of partially liquid phases in the area of the grain boundaries due to selective oxidation. However, the introduction of Ni into the alloy composition demonstrates a substantial improvement in crack mitigation. This finding emphasizes the importance of carefully managed tramp element content, particularly Cu and Sn in the continuous casting process to minimize crack formation during straightening but also indicates a strong influence of thermal history and bending temperatures.

AB - The decarbonization of steel production processes will lead to the increased use of scrap - including low-grade scrap - in the future. In addition to the more difficult control of some residuals in electric arc furnace steelmaking, tramp elements could also lead to problems in the manufacturing processes. In continuous casting, tramp elements such as Cu and Sn may cause network cracking and the so-called Cueq is still the most common indicator for surface defect susceptibility. This study addresses the experimental simulation of surface defect formation and the role of Cu, Sn, and Ni for the temperatures 900 and 1100 °C. Its goal is to define an optimized operational window for continuous casting. Experiments were conducted utilizing the in-situ material characterization by bending (IMC-B) test which characterizes the crack sensitivity of steel after controlled solidification and subsequent cooling under an adjustable water vapor atmosphere. The tests were performed on medium carbon steel with varying but moderate concentrations of Cu, Sn, and Ni. Results indicate that the simultaneous presence of Cu and Sn leads to a notable increase in the occurrence of surface cracks. This is attributable to the formation of partially liquid phases in the area of the grain boundaries due to selective oxidation. However, the introduction of Ni into the alloy composition demonstrates a substantial improvement in crack mitigation. This finding emphasizes the importance of carefully managed tramp element content, particularly Cu and Sn in the continuous casting process to minimize crack formation during straightening but also indicates a strong influence of thermal history and bending temperatures.

M3 - Conference contribution

BT - Proceedings of the 11th European Continuous Casting Conference 2024, Essen, Germany.

T2 - 10th European Continuous Casting Conference 2024

Y2 - 7 October 2024 through 11 October 2024

ER -