Strength determination for rough substrate-coating interfaces with three-dimensional defect structure
Research output: Contribution to journal › Article › Research › peer-review
Standard
In: International journal of refractory metals & hard materials, Vol. 2023, No. 112, 106149, 04.2023.
Research output: Contribution to journal › Article › Research › peer-review
Harvard
APA
Vancouver
Author
Bibtex - Download
}
RIS (suitable for import to EndNote) - Download
TY - JOUR
T1 - Strength determination for rough substrate-coating interfaces with three-dimensional defect structure
AU - Klünsner, Thomas
AU - Krobath, Martin
AU - Konetschnik, Ruth
AU - Tritremmel, Christian
AU - Maier-Kiener, Verena
AU - Samardzic, D.
AU - Ecker, Werner
AU - Czettl, Christoph
AU - Mitterer, Christian
AU - Kiener, Daniel
N1 - Publisher Copyright: © 2023 Elsevier Ltd
PY - 2023/4
Y1 - 2023/4
N2 - Quantitative information on the strength of interfaces between thin ceramic coatings and their substrates is crucial when aiming to understand their failure behavior. Many technically relevant substrate-coating interfaces are not ideally planar, but rather rough and contain stress concentrators forming three-dimensional defect structures. An example for such a realistic case, a polycrystalline diamond coating that partially penetrates voids and cavities in its Co binder-depleted WC-Co hard metal substrate, was investigated within the current work with respect to its unknown interface strength behavior. Special focus was laid on the influence of the applied load direction on the observed fracture behavior. Micromechanical specimens were produced via focused ion beam milling as geometry variants of a micro shear compression specimen with their loaded areas' relative inclination towards the substrate-coating interface varied from 0° to 88°. Specimen loading was performed until fracture with a flat punch indenter in a scanning electron microscope. The recorded fracture loads were associated with the spatial stress distributions at fracture via finite element-based analysis. A plateau of the determined maximum principal stress triggering fracture in the ceramic-ceramic interfaces was found for inclination angles ≥45°. This plateau value was identified as the interface strength by observation of the crack path at the substrate-coating interface via scanning electron microscopy and analysis of the effectively loaded interface area values. The presented novel material testing technique gives first and previously not accessible insight into the fracture behavior of rough substrate-coating interfaces with complex defect structure.
AB - Quantitative information on the strength of interfaces between thin ceramic coatings and their substrates is crucial when aiming to understand their failure behavior. Many technically relevant substrate-coating interfaces are not ideally planar, but rather rough and contain stress concentrators forming three-dimensional defect structures. An example for such a realistic case, a polycrystalline diamond coating that partially penetrates voids and cavities in its Co binder-depleted WC-Co hard metal substrate, was investigated within the current work with respect to its unknown interface strength behavior. Special focus was laid on the influence of the applied load direction on the observed fracture behavior. Micromechanical specimens were produced via focused ion beam milling as geometry variants of a micro shear compression specimen with their loaded areas' relative inclination towards the substrate-coating interface varied from 0° to 88°. Specimen loading was performed until fracture with a flat punch indenter in a scanning electron microscope. The recorded fracture loads were associated with the spatial stress distributions at fracture via finite element-based analysis. A plateau of the determined maximum principal stress triggering fracture in the ceramic-ceramic interfaces was found for inclination angles ≥45°. This plateau value was identified as the interface strength by observation of the crack path at the substrate-coating interface via scanning electron microscopy and analysis of the effectively loaded interface area values. The presented novel material testing technique gives first and previously not accessible insight into the fracture behavior of rough substrate-coating interfaces with complex defect structure.
UR - http://www.scopus.com/inward/record.url?scp=85147604817&partnerID=8YFLogxK
U2 - 10.1016/j.ijrmhm.2023.106149
DO - 10.1016/j.ijrmhm.2023.106149
M3 - Article
VL - 2023
JO - International journal of refractory metals & hard materials
JF - International journal of refractory metals & hard materials
SN - 0263-4368
IS - 112
M1 - 106149
ER -