Low-Cycle Fatigue Behavior of Wire and Arc Additively Manufactured Ti-6Al-4V Material

Research output: Contribution to journalArticleResearchpeer-review

Standard

Low-Cycle Fatigue Behavior of Wire and Arc Additively Manufactured Ti-6Al-4V Material. / Springer, Sebastian; Leitner, Martin; Gruber, Thomas et al.
In: Materials, Vol. 16.2023, No. 18, 6083, 05.09.2023.

Research output: Contribution to journalArticleResearchpeer-review

Author

Springer, Sebastian ; Leitner, Martin ; Gruber, Thomas et al. / Low-Cycle Fatigue Behavior of Wire and Arc Additively Manufactured Ti-6Al-4V Material. In: Materials. 2023 ; Vol. 16.2023, No. 18.

Bibtex - Download

@article{d1459a31235c4bb7aa8ba78838d814d8,
title = "Low-Cycle Fatigue Behavior of Wire and Arc Additively Manufactured Ti-6Al-4V Material",
abstract = "Additive manufacturing (AM) techniques, such as wire arc additive manufacturing (WAAM), offer unique advantages in producing large, complex structures with reduced lead time and material waste. However, their application in fatigue-critical applications requires a thorough understanding of the material properties and behavior. Due to the layered nature of the manufacturing process, WAAM structures have different microstructures and mechanical properties compared to their substrate counterparts. This study investigated the mechanical behavior and fatigue performance of Ti-6Al-4V fabricated using WAAM compared to the substrate material. Tensile and low-cycle fatigue (LCF) tests were conducted on both materials, and the microstructure was analyzed using optical microscopy and scanning electron microscopy (SEM). The results showed that the WAAM material has a coarser and more heterogeneous grain structure, an increased amount of defects, and lower ultimate tensile strength and smaller elongation at fracture. Furthermore, strain-controlled LCF tests revealed a lower fatigue strength of the WAAM material compared to the substrate, with crack initiation occurring at pores in the specimen rather than microstructural features. Experimental data were used to fit the Ramberg–Osgood model for cyclic deformation behavior and the Manson–Coffin–Basquin model for strain-life curves. The fitted models were subsequently used to compare the two material conditions with other AM processes. In general, the quasi-static properties of WAAM material were found to be lower than those of powder-based processes like selective laser melting or electron beam melting due to smaller cooling rates within the WAAM process. Finally, two simplified estimation models for the strain-life relationship were compared to the experimentally fitted Manson–Coffin–Basquin parameters. The results showed that the simple “universal material law” is applicable and can be used for a quick and simple estimation of the material behavior in cyclic loading conditions. Overall, this study highlights the importance of understanding the mechanical behavior and fatigue performance of WAAM structures compared to their substrate counterparts, as well as the need for further research to improve the understanding of the effects of WAAM process parameters on the mechanical properties and fatigue performance of the fabricated structures.",
keywords = "cyclic deformation, low-cycle fatigue, Manson–Coffin–Basquin, Ramberg–Osgood model, Ti-6Al-4V, wire arc additive manufacturing",
author = "Sebastian Springer and Martin Leitner and Thomas Gruber and Bernd Oberwinkler and Michael Lasnik and Florian Gr{\"u}n",
note = "Publisher Copyright: {\textcopyright} 2023 by the authors.",
year = "2023",
month = sep,
day = "5",
doi = "10.3390/ma16186083",
language = "English",
volume = "16.2023",
journal = " Materials",
issn = "1996-1944",
publisher = "Multidisciplinary Digital Publishing Institute (MDPI)",
number = "18",

}

RIS (suitable for import to EndNote) - Download

TY - JOUR

T1 - Low-Cycle Fatigue Behavior of Wire and Arc Additively Manufactured Ti-6Al-4V Material

AU - Springer, Sebastian

AU - Leitner, Martin

AU - Gruber, Thomas

AU - Oberwinkler, Bernd

AU - Lasnik, Michael

AU - Grün, Florian

N1 - Publisher Copyright: © 2023 by the authors.

PY - 2023/9/5

Y1 - 2023/9/5

N2 - Additive manufacturing (AM) techniques, such as wire arc additive manufacturing (WAAM), offer unique advantages in producing large, complex structures with reduced lead time and material waste. However, their application in fatigue-critical applications requires a thorough understanding of the material properties and behavior. Due to the layered nature of the manufacturing process, WAAM structures have different microstructures and mechanical properties compared to their substrate counterparts. This study investigated the mechanical behavior and fatigue performance of Ti-6Al-4V fabricated using WAAM compared to the substrate material. Tensile and low-cycle fatigue (LCF) tests were conducted on both materials, and the microstructure was analyzed using optical microscopy and scanning electron microscopy (SEM). The results showed that the WAAM material has a coarser and more heterogeneous grain structure, an increased amount of defects, and lower ultimate tensile strength and smaller elongation at fracture. Furthermore, strain-controlled LCF tests revealed a lower fatigue strength of the WAAM material compared to the substrate, with crack initiation occurring at pores in the specimen rather than microstructural features. Experimental data were used to fit the Ramberg–Osgood model for cyclic deformation behavior and the Manson–Coffin–Basquin model for strain-life curves. The fitted models were subsequently used to compare the two material conditions with other AM processes. In general, the quasi-static properties of WAAM material were found to be lower than those of powder-based processes like selective laser melting or electron beam melting due to smaller cooling rates within the WAAM process. Finally, two simplified estimation models for the strain-life relationship were compared to the experimentally fitted Manson–Coffin–Basquin parameters. The results showed that the simple “universal material law” is applicable and can be used for a quick and simple estimation of the material behavior in cyclic loading conditions. Overall, this study highlights the importance of understanding the mechanical behavior and fatigue performance of WAAM structures compared to their substrate counterparts, as well as the need for further research to improve the understanding of the effects of WAAM process parameters on the mechanical properties and fatigue performance of the fabricated structures.

AB - Additive manufacturing (AM) techniques, such as wire arc additive manufacturing (WAAM), offer unique advantages in producing large, complex structures with reduced lead time and material waste. However, their application in fatigue-critical applications requires a thorough understanding of the material properties and behavior. Due to the layered nature of the manufacturing process, WAAM structures have different microstructures and mechanical properties compared to their substrate counterparts. This study investigated the mechanical behavior and fatigue performance of Ti-6Al-4V fabricated using WAAM compared to the substrate material. Tensile and low-cycle fatigue (LCF) tests were conducted on both materials, and the microstructure was analyzed using optical microscopy and scanning electron microscopy (SEM). The results showed that the WAAM material has a coarser and more heterogeneous grain structure, an increased amount of defects, and lower ultimate tensile strength and smaller elongation at fracture. Furthermore, strain-controlled LCF tests revealed a lower fatigue strength of the WAAM material compared to the substrate, with crack initiation occurring at pores in the specimen rather than microstructural features. Experimental data were used to fit the Ramberg–Osgood model for cyclic deformation behavior and the Manson–Coffin–Basquin model for strain-life curves. The fitted models were subsequently used to compare the two material conditions with other AM processes. In general, the quasi-static properties of WAAM material were found to be lower than those of powder-based processes like selective laser melting or electron beam melting due to smaller cooling rates within the WAAM process. Finally, two simplified estimation models for the strain-life relationship were compared to the experimentally fitted Manson–Coffin–Basquin parameters. The results showed that the simple “universal material law” is applicable and can be used for a quick and simple estimation of the material behavior in cyclic loading conditions. Overall, this study highlights the importance of understanding the mechanical behavior and fatigue performance of WAAM structures compared to their substrate counterparts, as well as the need for further research to improve the understanding of the effects of WAAM process parameters on the mechanical properties and fatigue performance of the fabricated structures.

KW - cyclic deformation

KW - low-cycle fatigue

KW - Manson–Coffin–Basquin

KW - Ramberg–Osgood model

KW - Ti-6Al-4V

KW - wire arc additive manufacturing

UR - http://www.scopus.com/inward/record.url?scp=85173047942&partnerID=8YFLogxK

U2 - 10.3390/ma16186083

DO - 10.3390/ma16186083

M3 - Article

AN - SCOPUS:85173047942

VL - 16.2023

JO - Materials

JF - Materials

SN - 1996-1944

IS - 18

M1 - 6083

ER -