TY - JOUR

T1 - Investigations on the Triboelectrostatic Charging Behaviour and the Triboelectrostatic Sortability of Different Oxides

AU - Gehringer, Sabrina

AU - Luckeneder, Christoph

AU - Flachberger, Helmut

PY - 2020/10/14

Y1 - 2020/10/14

N2 - In the course of this study, several test series were carried out to investigate the triboelectrostatic charging behaviour of various oxides. At the beginning, the influence of the degree of aging and the influence of the sample storage on the charging efficiency of the oxide samples was analysed. For this purpose, two oxide samples were stored under different environmental conditions and then sorted using triboelectrostatic belt separation. Results of a previous series of tests showed that an increased feed temperature has a negative effect on the charging behaviour of calcium and magnesium oxide. Therefore, the effects of a reduced feed temperature were also examined. For these experiments, samples were stored at 8 °C under exclusion of air. In addition, a series of tests was carried out with a gradual increase of the voltage on the triboelectrostatic belt separator in order to determine possible differences in the charging efficiency of calcium oxide and magnesium oxide and to subsequently use them for the separation.

AB - In the course of this study, several test series were carried out to investigate the triboelectrostatic charging behaviour of various oxides. At the beginning, the influence of the degree of aging and the influence of the sample storage on the charging efficiency of the oxide samples was analysed. For this purpose, two oxide samples were stored under different environmental conditions and then sorted using triboelectrostatic belt separation. Results of a previous series of tests showed that an increased feed temperature has a negative effect on the charging behaviour of calcium and magnesium oxide. Therefore, the effects of a reduced feed temperature were also examined. For these experiments, samples were stored at 8 °C under exclusion of air. In addition, a series of tests was carried out with a gradual increase of the voltage on the triboelectrostatic belt separator in order to determine possible differences in the charging efficiency of calcium oxide and magnesium oxide and to subsequently use them for the separation.

U2 - 10.1007/s00501-020-01025-7

DO - 10.1007/s00501-020-01025-7

M3 - Article

VL - 165.2020

SP - 525

EP - 531

JO - Berg- und hüttenmännische Monatshefte : BHM

JF - Berg- und hüttenmännische Monatshefte : BHM

SN - 0005-8912

IS - 10

ER -