Influence of Microalloying Elements on the Precipitation Behaviour of Aluminium Alloys

Research output: Contribution to conferencePresentationResearch

Standard

Influence of Microalloying Elements on the Precipitation Behaviour of Aluminium Alloys. / Werinos, Marion; Antrekowitsch, Helmut.
2013. European Metallurgical Conference 2013, Weimar, Germany.

Research output: Contribution to conferencePresentationResearch

Harvard

Werinos, M & Antrekowitsch, H 2013, 'Influence of Microalloying Elements on the Precipitation Behaviour of Aluminium Alloys', European Metallurgical Conference 2013, Weimar, Germany, 23/06/13 - 26/06/13.

Vancouver

Bibtex - Download

@conference{d5c237f7256c4e54a2abc85d2d1be832,
title = "Influence of Microalloying Elements on the Precipitation Behaviour of Aluminium Alloys",
abstract = "Al-Mg-Si alloys are widely used in cast, wrought and extruded form. A characteristic property of these alloys is the negative effect of natural pre-aging at room temperature on artificial aging. Minor additions of Sn suppress the adverse effect of room temperature aging due to controlled buffering of quenched-in excess vacancies at low temperatures. In this study we evaluate the buffering performance of Sn in the temperature range between 5 and 45 °C. This is investigated for two Sn-added AA6061 alloys with systematic variation in their Mg-, Si- and Cu-content, for comparison the natural aging kinetics of a Sn-free alloy is studied. In general a strong dependence of hardening kinetics on temperature and on chemical composition is observed. Results of aging kinetics are discussed in terms of common clustering theories and calculations of the temperature dependent trapping effect of Sn on excess vacancies.",
author = "Marion Werinos and Helmut Antrekowitsch",
year = "2013",
month = jun,
day = "24",
language = "English",
note = "European Metallurgical Conference 2013 ; Conference date: 23-06-2013 Through 26-06-2013",

}

RIS (suitable for import to EndNote) - Download

TY - CONF

T1 - Influence of Microalloying Elements on the Precipitation Behaviour of Aluminium Alloys

AU - Werinos, Marion

AU - Antrekowitsch, Helmut

PY - 2013/6/24

Y1 - 2013/6/24

N2 - Al-Mg-Si alloys are widely used in cast, wrought and extruded form. A characteristic property of these alloys is the negative effect of natural pre-aging at room temperature on artificial aging. Minor additions of Sn suppress the adverse effect of room temperature aging due to controlled buffering of quenched-in excess vacancies at low temperatures. In this study we evaluate the buffering performance of Sn in the temperature range between 5 and 45 °C. This is investigated for two Sn-added AA6061 alloys with systematic variation in their Mg-, Si- and Cu-content, for comparison the natural aging kinetics of a Sn-free alloy is studied. In general a strong dependence of hardening kinetics on temperature and on chemical composition is observed. Results of aging kinetics are discussed in terms of common clustering theories and calculations of the temperature dependent trapping effect of Sn on excess vacancies.

AB - Al-Mg-Si alloys are widely used in cast, wrought and extruded form. A characteristic property of these alloys is the negative effect of natural pre-aging at room temperature on artificial aging. Minor additions of Sn suppress the adverse effect of room temperature aging due to controlled buffering of quenched-in excess vacancies at low temperatures. In this study we evaluate the buffering performance of Sn in the temperature range between 5 and 45 °C. This is investigated for two Sn-added AA6061 alloys with systematic variation in their Mg-, Si- and Cu-content, for comparison the natural aging kinetics of a Sn-free alloy is studied. In general a strong dependence of hardening kinetics on temperature and on chemical composition is observed. Results of aging kinetics are discussed in terms of common clustering theories and calculations of the temperature dependent trapping effect of Sn on excess vacancies.