Hardness Loss of Plastic Mold Steels: Phenomenon in Injection Molding

Research output: Contribution to journalArticleResearchpeer-review

Standard

Hardness Loss of Plastic Mold Steels: Phenomenon in Injection Molding. / Zidar, David; Landefeld, Andreas; Gschöpf, Boris et al.
In: Steel research international, Vol. 94.2022, No. 4, 2200326, 28.09.2022.

Research output: Contribution to journalArticleResearchpeer-review

Bibtex - Download

@article{4ecd30b12fc34392b904b4fc6d5c2d04,
title = "Hardness Loss of Plastic Mold Steels: Phenomenon in Injection Molding",
abstract = "The standard application-oriented test for abrasive wear of polymers on plastic mold steels is the platelet wear tester method in which two steel specimens form a thin wear slit. The glass fiber-reinforced polymer melt is injected through the wear slit, and the surface of both specimens is abraded. In the injection molding process, similar conditions often occur in thin-walled parts or film gates. Drastic loss of the hardness of a powder metallurgical steel (PM steel) is discovered after approx. 200 injection cycles while performing platelet wear tests. For experimentally analyzing the reason for the loss of steel hardness during injection molding, a new platelet wear testing apparatus is developed, which can be used to measure the increase in temperature inside the steel specimen while testing. The first results show and support the hypothesis that a temperature increase above the annealing temperature occurs inside the steel due to viscous dissipation at the steel surface. In cooperation with the company voestalpine B{\"O}HLER Edelstahl & Co KG, tests on the PM steel in a dilatometer are performed to simulate the cycle-by-cycle heat pulses occurring in the injection molding process. With the results of those tests, it is possible to state a hypothesis for the reason of this hardness loss.",
author = "David Zidar and Andreas Landefeld and Boris Gsch{\"o}pf and Ronald Schnitzer and Horst Zunko and Walter Friesenbichler",
year = "2022",
month = sep,
day = "28",
doi = "10.1002/srin.202200326",
language = "English",
volume = "94.2022",
journal = "Steel research international",
issn = "0177-4832",
publisher = "Verlag Stahleisen GmbH",
number = "4",

}

RIS (suitable for import to EndNote) - Download

TY - JOUR

T1 - Hardness Loss of Plastic Mold Steels

T2 - Phenomenon in Injection Molding

AU - Zidar, David

AU - Landefeld, Andreas

AU - Gschöpf, Boris

AU - Schnitzer, Ronald

AU - Zunko, Horst

AU - Friesenbichler, Walter

PY - 2022/9/28

Y1 - 2022/9/28

N2 - The standard application-oriented test for abrasive wear of polymers on plastic mold steels is the platelet wear tester method in which two steel specimens form a thin wear slit. The glass fiber-reinforced polymer melt is injected through the wear slit, and the surface of both specimens is abraded. In the injection molding process, similar conditions often occur in thin-walled parts or film gates. Drastic loss of the hardness of a powder metallurgical steel (PM steel) is discovered after approx. 200 injection cycles while performing platelet wear tests. For experimentally analyzing the reason for the loss of steel hardness during injection molding, a new platelet wear testing apparatus is developed, which can be used to measure the increase in temperature inside the steel specimen while testing. The first results show and support the hypothesis that a temperature increase above the annealing temperature occurs inside the steel due to viscous dissipation at the steel surface. In cooperation with the company voestalpine BÖHLER Edelstahl & Co KG, tests on the PM steel in a dilatometer are performed to simulate the cycle-by-cycle heat pulses occurring in the injection molding process. With the results of those tests, it is possible to state a hypothesis for the reason of this hardness loss.

AB - The standard application-oriented test for abrasive wear of polymers on plastic mold steels is the platelet wear tester method in which two steel specimens form a thin wear slit. The glass fiber-reinforced polymer melt is injected through the wear slit, and the surface of both specimens is abraded. In the injection molding process, similar conditions often occur in thin-walled parts or film gates. Drastic loss of the hardness of a powder metallurgical steel (PM steel) is discovered after approx. 200 injection cycles while performing platelet wear tests. For experimentally analyzing the reason for the loss of steel hardness during injection molding, a new platelet wear testing apparatus is developed, which can be used to measure the increase in temperature inside the steel specimen while testing. The first results show and support the hypothesis that a temperature increase above the annealing temperature occurs inside the steel due to viscous dissipation at the steel surface. In cooperation with the company voestalpine BÖHLER Edelstahl & Co KG, tests on the PM steel in a dilatometer are performed to simulate the cycle-by-cycle heat pulses occurring in the injection molding process. With the results of those tests, it is possible to state a hypothesis for the reason of this hardness loss.

U2 - 10.1002/srin.202200326

DO - 10.1002/srin.202200326

M3 - Article

VL - 94.2022

JO - Steel research international

JF - Steel research international

SN - 0177-4832

IS - 4

M1 - 2200326

ER -