Fatigue crack growth anisotropy in ultrafine-grained iron
Research output: Contribution to journal › Article › Research › peer-review
Standard
In: Acta materialia, Vol. 126.2017, No. March, 01.03.2017, p. 154-165.
Research output: Contribution to journal › Article › Research › peer-review
Harvard
APA
Vancouver
Author
Bibtex - Download
}
RIS (suitable for import to EndNote) - Download
TY - JOUR
T1 - Fatigue crack growth anisotropy in ultrafine-grained iron
AU - Leitner, Thomas
AU - Hohenwarter, Anton
AU - Ochensberger, Walter
AU - Pippan, Reinhard
PY - 2017/3/1
Y1 - 2017/3/1
N2 - Nanocrystalline and ultrafine-grained (UFG) metals produced by severe plastic deformation exhibit often microstructures with elongated grains, which result in orientation dependent mechanical properties. This anisotropy is especially pronounced for the resistance against quasi-static and cyclic crack growth. In order to gain more knowledge about the consequences of anisotropic microstructures in the case of cyclic loading, fatigue crack growth (FCG) experiments were performed on UFG iron processed by high pressure torsion, with a mean grain size of 500 × 400 × 150 nm3. Samples with four different orientations were prepared and tested with two mean stresses to account for crack closure effects. The FCG rate varies by one order of magnitude between cracks propagating parallel to elongated grains and cracks advancing perpendicular to it. This larger difference is discussed in the light of intrinsic and extrinsic toughening mechanisms. It is concluded that crack closure contributions are reduced in UFG Fe, however, geometric shielding due to more frequently occurring crack branching leads to a significantly higher FCG resistance for cracks perpendicular to the grain elongation. Furthermore, it is observed that grain refinement leads to a transition from transgranular to intergranular fracture. However, it can be shown that this intergranular crack growth of UFG iron under cyclic loading is not the result of grain boundary embrittlement, but occurs due to a blunting and re-sharpening process along the grain boundaries.
AB - Nanocrystalline and ultrafine-grained (UFG) metals produced by severe plastic deformation exhibit often microstructures with elongated grains, which result in orientation dependent mechanical properties. This anisotropy is especially pronounced for the resistance against quasi-static and cyclic crack growth. In order to gain more knowledge about the consequences of anisotropic microstructures in the case of cyclic loading, fatigue crack growth (FCG) experiments were performed on UFG iron processed by high pressure torsion, with a mean grain size of 500 × 400 × 150 nm3. Samples with four different orientations were prepared and tested with two mean stresses to account for crack closure effects. The FCG rate varies by one order of magnitude between cracks propagating parallel to elongated grains and cracks advancing perpendicular to it. This larger difference is discussed in the light of intrinsic and extrinsic toughening mechanisms. It is concluded that crack closure contributions are reduced in UFG Fe, however, geometric shielding due to more frequently occurring crack branching leads to a significantly higher FCG resistance for cracks perpendicular to the grain elongation. Furthermore, it is observed that grain refinement leads to a transition from transgranular to intergranular fracture. However, it can be shown that this intergranular crack growth of UFG iron under cyclic loading is not the result of grain boundary embrittlement, but occurs due to a blunting and re-sharpening process along the grain boundaries.
KW - Anisotropy
KW - Crack closure
KW - Crack deflection
KW - Fatigue crack propagation
KW - Ultrafine-grained materials
UR - http://www.scopus.com/inward/record.url?scp=85007480710&partnerID=8YFLogxK
U2 - 10.1016/j.actamat.2016.12.059
DO - 10.1016/j.actamat.2016.12.059
M3 - Article
AN - SCOPUS:85007480710
VL - 126.2017
SP - 154
EP - 165
JO - Acta materialia
JF - Acta materialia
SN - 1359-6454
IS - March
ER -