Emissivity measurements conducted on intermetallic γ-TiAl-based alloys for aeronautical applications

Research output: Contribution to journalArticleResearchpeer-review

Standard

Emissivity measurements conducted on intermetallic γ-TiAl-based alloys for aeronautical applications. / Usategui, Leire; López-Ferreno, I.; Echániz, T. et al.
In: Journal of Materials Research and Technology, Vol. 27.2023, No. November-December, 01.11.2023, p. 3170-3179.

Research output: Contribution to journalArticleResearchpeer-review

Harvard

Usategui, L, López-Ferreno, I, Echániz, T, Sainz-Menchón, M, Musi, M, Clemens, H & López, GA 2023, 'Emissivity measurements conducted on intermetallic γ-TiAl-based alloys for aeronautical applications', Journal of Materials Research and Technology, vol. 27.2023, no. November-December, pp. 3170-3179. https://doi.org/10.1016/j.jmrt.2023.10.163

APA

Vancouver

Usategui L, López-Ferreno I, Echániz T, Sainz-Menchón M, Musi M, Clemens H et al. Emissivity measurements conducted on intermetallic γ-TiAl-based alloys for aeronautical applications. Journal of Materials Research and Technology. 2023 Nov 1;27.2023(November-December):3170-3179. Epub 2023 Oct 19. doi: 10.1016/j.jmrt.2023.10.163

Author

Usategui, Leire ; López-Ferreno, I. ; Echániz, T. et al. / Emissivity measurements conducted on intermetallic γ-TiAl-based alloys for aeronautical applications. In: Journal of Materials Research and Technology. 2023 ; Vol. 27.2023, No. November-December. pp. 3170-3179.

Bibtex - Download

@article{1d5297c7822a4b8f960720ba34d45cb0,
title = "Emissivity measurements conducted on intermetallic γ-TiAl-based alloys for aeronautical applications",
abstract = "The directional spectral emissivity of a Ti–48Al–2Nb–2Cr alloy (in at.%), 4822 alloy, and a Ti-43.5Al–4Nb–1Mo-0.1B alloy (in at.%),TNM alloy, used in the aeronautical industry, are measured between 150 and 850 °C. The differences in the emissivity values between both alloys at the lowest temperatures, indicates that the βo phase, only present in TNM, exhibit higher emissivity values. By numerical integration of the measured data, the total directional and hemispherical emissivity have been calculated. At 850 °C the total hemispherical emissivity in vacuum are nearly identical with 0.274 ± 0.006 for the 4822 alloy and 0.273 ± 0.007 for the TNM alloy. The lower emissivity change with temperature measured in TNM alloys is related with the deconvolution of βo phase by diffusion processes. Afterwards, near-normal spectral emissivity measurements are performed in both alloys during isothermal oxidation treatments at 750 °C and 850 °C for 120 h. The emissivity data reveal that the TNM alloy exhibits higher oxidation resistance especially at 750 °C. In parallel, microstructural characterization has been performed before the measurements, after the directional emissivity measurements prior to oxidation and after isothermal oxidations. The formed oxide scale is composed of four layers that coincide with those reported in the literature: an outer layer of TiO2 contiguous with a layer of Al2O3, followed by a TiO2/Al2O3 mixed layer and finally a thin layer of Nb-rich nitride. This mixed layer governs the interferential part of the alloys{\textquoteright} emissivity spectra, which, in combination with the background, determines the overall radiative behavior of the alloys under service conditions.",
author = "Leire Usategui and I. L{\'o}pez-Ferreno and T. Ech{\'a}niz and M. Sainz-Mench{\'o}n and Michael Musi and Helmut Clemens and G.A. L{\'o}pez",
note = "Publisher Copyright: {\textcopyright} 2023 The Authors",
year = "2023",
month = nov,
day = "1",
doi = "10.1016/j.jmrt.2023.10.163",
language = "English",
volume = "27.2023",
pages = "3170--3179",
journal = "Journal of Materials Research and Technology",
issn = "2238-7854",
publisher = "Elsevier",
number = "November-December",

}

RIS (suitable for import to EndNote) - Download

TY - JOUR

T1 - Emissivity measurements conducted on intermetallic γ-TiAl-based alloys for aeronautical applications

AU - Usategui, Leire

AU - López-Ferreno, I.

AU - Echániz, T.

AU - Sainz-Menchón, M.

AU - Musi, Michael

AU - Clemens, Helmut

AU - López, G.A.

N1 - Publisher Copyright: © 2023 The Authors

PY - 2023/11/1

Y1 - 2023/11/1

N2 - The directional spectral emissivity of a Ti–48Al–2Nb–2Cr alloy (in at.%), 4822 alloy, and a Ti-43.5Al–4Nb–1Mo-0.1B alloy (in at.%),TNM alloy, used in the aeronautical industry, are measured between 150 and 850 °C. The differences in the emissivity values between both alloys at the lowest temperatures, indicates that the βo phase, only present in TNM, exhibit higher emissivity values. By numerical integration of the measured data, the total directional and hemispherical emissivity have been calculated. At 850 °C the total hemispherical emissivity in vacuum are nearly identical with 0.274 ± 0.006 for the 4822 alloy and 0.273 ± 0.007 for the TNM alloy. The lower emissivity change with temperature measured in TNM alloys is related with the deconvolution of βo phase by diffusion processes. Afterwards, near-normal spectral emissivity measurements are performed in both alloys during isothermal oxidation treatments at 750 °C and 850 °C for 120 h. The emissivity data reveal that the TNM alloy exhibits higher oxidation resistance especially at 750 °C. In parallel, microstructural characterization has been performed before the measurements, after the directional emissivity measurements prior to oxidation and after isothermal oxidations. The formed oxide scale is composed of four layers that coincide with those reported in the literature: an outer layer of TiO2 contiguous with a layer of Al2O3, followed by a TiO2/Al2O3 mixed layer and finally a thin layer of Nb-rich nitride. This mixed layer governs the interferential part of the alloys’ emissivity spectra, which, in combination with the background, determines the overall radiative behavior of the alloys under service conditions.

AB - The directional spectral emissivity of a Ti–48Al–2Nb–2Cr alloy (in at.%), 4822 alloy, and a Ti-43.5Al–4Nb–1Mo-0.1B alloy (in at.%),TNM alloy, used in the aeronautical industry, are measured between 150 and 850 °C. The differences in the emissivity values between both alloys at the lowest temperatures, indicates that the βo phase, only present in TNM, exhibit higher emissivity values. By numerical integration of the measured data, the total directional and hemispherical emissivity have been calculated. At 850 °C the total hemispherical emissivity in vacuum are nearly identical with 0.274 ± 0.006 for the 4822 alloy and 0.273 ± 0.007 for the TNM alloy. The lower emissivity change with temperature measured in TNM alloys is related with the deconvolution of βo phase by diffusion processes. Afterwards, near-normal spectral emissivity measurements are performed in both alloys during isothermal oxidation treatments at 750 °C and 850 °C for 120 h. The emissivity data reveal that the TNM alloy exhibits higher oxidation resistance especially at 750 °C. In parallel, microstructural characterization has been performed before the measurements, after the directional emissivity measurements prior to oxidation and after isothermal oxidations. The formed oxide scale is composed of four layers that coincide with those reported in the literature: an outer layer of TiO2 contiguous with a layer of Al2O3, followed by a TiO2/Al2O3 mixed layer and finally a thin layer of Nb-rich nitride. This mixed layer governs the interferential part of the alloys’ emissivity spectra, which, in combination with the background, determines the overall radiative behavior of the alloys under service conditions.

UR - http://www.scopus.com/inward/record.url?scp=85174816615&partnerID=8YFLogxK

U2 - 10.1016/j.jmrt.2023.10.163

DO - 10.1016/j.jmrt.2023.10.163

M3 - Article

VL - 27.2023

SP - 3170

EP - 3179

JO - Journal of Materials Research and Technology

JF - Journal of Materials Research and Technology

SN - 2238-7854

IS - November-December

ER -