Revealing nucleation kinetics of entrained eutectic Si droplets in high purity melt spun Al-5Si based alloys with additions of Ta, TiB2, Eu and P

Publikationen: Beitrag in FachzeitschriftArtikelForschung(peer-reviewed)

Standard

Revealing nucleation kinetics of entrained eutectic Si droplets in high purity melt spun Al-5Si based alloys with additions of Ta, TiB2, Eu and P. / Spáčil, Ivo; LI, Jiehua.
in: Journal of alloys and compounds, Jahrgang 968.2023, Nr. 15 December, 172032, 15.12.2023.

Publikationen: Beitrag in FachzeitschriftArtikelForschung(peer-reviewed)

Bibtex - Download

@article{8d17dd8a07e845b692fb5064a2b37665,
title = "Revealing nucleation kinetics of entrained eutectic Si droplets in high purity melt spun Al-5Si based alloys with additions of Ta, TiB2, Eu and P",
abstract = "High purity (HP) Al-5 wt% Si with additions of Ta, TiB 2, Eu and P were produced by arc melting and melt-spinning. Nucleation kinetics of entrained eutectic Si droplets in HP melt spun Al-5Si based alloys was investigated using differential scanning calorimetry (DSC), scanning electron microscopy (SEM), electron backscatter diffraction (EBSD) and transmission electron microscopy (TEM). No significant effect of Ta and/or TiB 2 on nucleation kinetics and microstructure of entrained eutectic Si droplets was observed, although Al 3Ta was observed at hyperperitectic concentrations. In contrast, a significant effect of Eu and/or P on nucleation kinetics and microstructure of entrained eutectic Si droplets was observed. Increasing P concentration increases the onset temperature and exhibits a lower undercooling required for the nucleation of entrained eutectic Si droplets. Large Al 2Si 2Eu phase was observed both within the Al matrix and along the boundaries of entrained eutectic Si droplets, while small Al 2Si 2Eu phase was also observed within entrained eutectic Si droplets. With increasing P, EBSD reveals the transition from fine randomly multiply-oriented fibrous eutectic Si to coarse single-oriented plate eutectic Si within the entrained eutectic Si droplets. With further increasing P, fewer coarse Si crystals were observed within the entrained eutectic Si droplets. EBSD indicates that the entrained eutectic Si droplet can be nucleated from AlP nucleation site.",
author = "Ivo Sp{\'a}{\v c}il and Jiehua LI",
note = "Publisher Copyright: {\textcopyright} 2023",
year = "2023",
month = dec,
day = "15",
doi = "10.1016/j.jallcom.2023.172032",
language = "English",
volume = "968.2023",
journal = "Journal of alloys and compounds",
issn = "0925-8388",
publisher = "Elsevier",
number = "15 December",

}

RIS (suitable for import to EndNote) - Download

TY - JOUR

T1 - Revealing nucleation kinetics of entrained eutectic Si droplets in high purity melt spun Al-5Si based alloys with additions of Ta, TiB2, Eu and P

AU - Spáčil, Ivo

AU - LI, Jiehua

N1 - Publisher Copyright: © 2023

PY - 2023/12/15

Y1 - 2023/12/15

N2 - High purity (HP) Al-5 wt% Si with additions of Ta, TiB 2, Eu and P were produced by arc melting and melt-spinning. Nucleation kinetics of entrained eutectic Si droplets in HP melt spun Al-5Si based alloys was investigated using differential scanning calorimetry (DSC), scanning electron microscopy (SEM), electron backscatter diffraction (EBSD) and transmission electron microscopy (TEM). No significant effect of Ta and/or TiB 2 on nucleation kinetics and microstructure of entrained eutectic Si droplets was observed, although Al 3Ta was observed at hyperperitectic concentrations. In contrast, a significant effect of Eu and/or P on nucleation kinetics and microstructure of entrained eutectic Si droplets was observed. Increasing P concentration increases the onset temperature and exhibits a lower undercooling required for the nucleation of entrained eutectic Si droplets. Large Al 2Si 2Eu phase was observed both within the Al matrix and along the boundaries of entrained eutectic Si droplets, while small Al 2Si 2Eu phase was also observed within entrained eutectic Si droplets. With increasing P, EBSD reveals the transition from fine randomly multiply-oriented fibrous eutectic Si to coarse single-oriented plate eutectic Si within the entrained eutectic Si droplets. With further increasing P, fewer coarse Si crystals were observed within the entrained eutectic Si droplets. EBSD indicates that the entrained eutectic Si droplet can be nucleated from AlP nucleation site.

AB - High purity (HP) Al-5 wt% Si with additions of Ta, TiB 2, Eu and P were produced by arc melting and melt-spinning. Nucleation kinetics of entrained eutectic Si droplets in HP melt spun Al-5Si based alloys was investigated using differential scanning calorimetry (DSC), scanning electron microscopy (SEM), electron backscatter diffraction (EBSD) and transmission electron microscopy (TEM). No significant effect of Ta and/or TiB 2 on nucleation kinetics and microstructure of entrained eutectic Si droplets was observed, although Al 3Ta was observed at hyperperitectic concentrations. In contrast, a significant effect of Eu and/or P on nucleation kinetics and microstructure of entrained eutectic Si droplets was observed. Increasing P concentration increases the onset temperature and exhibits a lower undercooling required for the nucleation of entrained eutectic Si droplets. Large Al 2Si 2Eu phase was observed both within the Al matrix and along the boundaries of entrained eutectic Si droplets, while small Al 2Si 2Eu phase was also observed within entrained eutectic Si droplets. With increasing P, EBSD reveals the transition from fine randomly multiply-oriented fibrous eutectic Si to coarse single-oriented plate eutectic Si within the entrained eutectic Si droplets. With further increasing P, fewer coarse Si crystals were observed within the entrained eutectic Si droplets. EBSD indicates that the entrained eutectic Si droplet can be nucleated from AlP nucleation site.

UR - http://www.scopus.com/inward/record.url?scp=85170419674&partnerID=8YFLogxK

U2 - 10.1016/j.jallcom.2023.172032

DO - 10.1016/j.jallcom.2023.172032

M3 - Article

VL - 968.2023

JO - Journal of alloys and compounds

JF - Journal of alloys and compounds

SN - 0925-8388

IS - 15 December

M1 - 172032

ER -