Perovskite-Type Oxide Catalysts in CO2 Utilization: A Principal Study of Novel Cu-Doped Perovskites for Methanol Synthesis

Publikationen: Beitrag in FachzeitschriftArtikelForschung(peer-reviewed)

Standard

Perovskite-Type Oxide Catalysts in CO2 Utilization: A Principal Study of Novel Cu-Doped Perovskites for Methanol Synthesis. / Schrenk, Florian; Lindenthal, Lorenz; Pacholik, Gernot et al.
in: Compounds, Jahrgang 2:2022, Nr. 4, 14.12.2022, S. 378-387.

Publikationen: Beitrag in FachzeitschriftArtikelForschung(peer-reviewed)

Vancouver

Bibtex - Download

@article{81ac93461bc4432792b8589aa8095271,
title = "Perovskite-Type Oxide Catalysts in CO2 Utilization: A Principal Study of Novel Cu-Doped Perovskites for Methanol Synthesis",
abstract = "Six different perovskite-type oxides were investigated with respect to their ability for methanol synthesis via H2 and CO2: Fe-, Mn-, and Ti-based perovskites were prepared with and without Cu doping. For assessment, the catalysts were subjected to preliminary tests at atmospheric pressure to evaluate their ability to activate CO2. Additional catalytic tests with the doped versions of each catalyst type were carried out in a pressured reactor at 21 bar. After the measurements, the catalysts were characterized with X-ray diffraction (XRD) and scanning electron microscopy (SEM). All catalysts were able to produce methanol in the pressure tests. CO2 conversions between 14% and 23% were reached at 400 °C, with the highest methanol selectivity at the lower temperature of 250 °C. The combination of XRD and SEM revealed that the Fe-based and Ti-based perovskites were stable under reaction conditions and that catalytically highly active and stable nanoparticles had formed. The minor formation of CaCO3, which is a deactivating phase, was observed for one catalyst. These nanoparticles showed resistance to coking and sintering. However, the yield and selectivity for methanol need to be improved via the further tailoring of the perovskite composition.",
author = "Florian Schrenk and Lorenz Lindenthal and Gernot Pacholik and Tina Navratil and Berger, {Tobias Maximilian} and Hedda Drexler and Raffael Rameshan and Thomas Ruh and Karin F{\"o}ttinger and Christoph Rameshan",
year = "2022",
month = dec,
day = "14",
doi = "10.3390/compounds2040031",
language = "English",
volume = "2:2022",
pages = "378--387",
journal = "Compounds",
issn = "2673-6918",
publisher = "Multidisciplinary Digital Publishing Institute (MDPI)",
number = "4",

}

RIS (suitable for import to EndNote) - Download

TY - JOUR

T1 - Perovskite-Type Oxide Catalysts in CO2 Utilization: A Principal Study of Novel Cu-Doped Perovskites for Methanol Synthesis

AU - Schrenk, Florian

AU - Lindenthal, Lorenz

AU - Pacholik, Gernot

AU - Navratil, Tina

AU - Berger, Tobias Maximilian

AU - Drexler, Hedda

AU - Rameshan, Raffael

AU - Ruh, Thomas

AU - Föttinger, Karin

AU - Rameshan, Christoph

PY - 2022/12/14

Y1 - 2022/12/14

N2 - Six different perovskite-type oxides were investigated with respect to their ability for methanol synthesis via H2 and CO2: Fe-, Mn-, and Ti-based perovskites were prepared with and without Cu doping. For assessment, the catalysts were subjected to preliminary tests at atmospheric pressure to evaluate their ability to activate CO2. Additional catalytic tests with the doped versions of each catalyst type were carried out in a pressured reactor at 21 bar. After the measurements, the catalysts were characterized with X-ray diffraction (XRD) and scanning electron microscopy (SEM). All catalysts were able to produce methanol in the pressure tests. CO2 conversions between 14% and 23% were reached at 400 °C, with the highest methanol selectivity at the lower temperature of 250 °C. The combination of XRD and SEM revealed that the Fe-based and Ti-based perovskites were stable under reaction conditions and that catalytically highly active and stable nanoparticles had formed. The minor formation of CaCO3, which is a deactivating phase, was observed for one catalyst. These nanoparticles showed resistance to coking and sintering. However, the yield and selectivity for methanol need to be improved via the further tailoring of the perovskite composition.

AB - Six different perovskite-type oxides were investigated with respect to their ability for methanol synthesis via H2 and CO2: Fe-, Mn-, and Ti-based perovskites were prepared with and without Cu doping. For assessment, the catalysts were subjected to preliminary tests at atmospheric pressure to evaluate their ability to activate CO2. Additional catalytic tests with the doped versions of each catalyst type were carried out in a pressured reactor at 21 bar. After the measurements, the catalysts were characterized with X-ray diffraction (XRD) and scanning electron microscopy (SEM). All catalysts were able to produce methanol in the pressure tests. CO2 conversions between 14% and 23% were reached at 400 °C, with the highest methanol selectivity at the lower temperature of 250 °C. The combination of XRD and SEM revealed that the Fe-based and Ti-based perovskites were stable under reaction conditions and that catalytically highly active and stable nanoparticles had formed. The minor formation of CaCO3, which is a deactivating phase, was observed for one catalyst. These nanoparticles showed resistance to coking and sintering. However, the yield and selectivity for methanol need to be improved via the further tailoring of the perovskite composition.

U2 - 10.3390/compounds2040031

DO - 10.3390/compounds2040031

M3 - Article

VL - 2:2022

SP - 378

EP - 387

JO - Compounds

JF - Compounds

SN - 2673-6918

IS - 4

ER -