Microstructure and Tensile Properties of AZ61 Alloy Sheets Processed by High-Ratio Extrusion with Subsequent Direct Aging Treatment

Publikationen: Beitrag in FachzeitschriftArtikelForschung(peer-reviewed)

Standard

Microstructure and Tensile Properties of AZ61 Alloy Sheets Processed by High-Ratio Extrusion with Subsequent Direct Aging Treatment. / Zhang, Cheng-Cheng; Wang, Hui-Yuan; Zha, Min et al.
in: Materials, Jahrgang 11.2018, Nr. 6, 895, 26.05.2018.

Publikationen: Beitrag in FachzeitschriftArtikelForschung(peer-reviewed)

Vancouver

Zhang CC, Wang HY, Zha M, Wang C, Li JH, Yang ZZ et al. Microstructure and Tensile Properties of AZ61 Alloy Sheets Processed by High-Ratio Extrusion with Subsequent Direct Aging Treatment. Materials. 2018 Mai 26;11.2018(6):895. doi: 10.3390/ma11060895

Author

Zhang, Cheng-Cheng ; Wang, Hui-Yuan ; Zha, Min et al. / Microstructure and Tensile Properties of AZ61 Alloy Sheets Processed by High-Ratio Extrusion with Subsequent Direct Aging Treatment. in: Materials. 2018 ; Jahrgang 11.2018, Nr. 6.

Bibtex - Download

@article{9d95730f28ab4d2b9c2eb2b89155577b,
title = "Microstructure and Tensile Properties of AZ61 Alloy Sheets Processed by High-Ratio Extrusion with Subsequent Direct Aging Treatment",
abstract = "A high extrusion ratio of 166:1 was applied to commercial AZ61 alloy in one step with an extrusion speed of 2.1 m·min−1. The effects of DA (direct aging) treatment on the microstructure and tensile properties of extruded alloy were investigated. The extruded alloy exhibits fine DRXed grains and the average grain size is ~11 μm. After DA treatment at 170 °C, the tensile strength and 0.2% offset yield strength is enhanced from 314 to 336 MPa and from 169 to 191 MPa respectively, sacrificing elongation from 26.5% to 23.3%. The grain size and texture distribution of extruded AZ61 scarcely evolve during the post aging treatment. However, the enhanced strength in peak-aged alloy is mainly caused by the high-density elliptical Mg17Al12 precipitates distributing uniformly along the grain boundaries or within the grains, by precipitation and dispersion hardening. Furthermore, the nano-sized precipitates effectively inhibit grains from coarsening by triggering pinning effects along the grain boundaries at elevated temperature. As a result, the peak-aged alloy exhibits a better superplasticity of 306.5% compared with that of 231.8% of extruded sample. This work provides a practical one-step method for mass-producing Mg alloy sheets with excellent tensile strength and ductility compared with those fabricated by conventional extrusion methods.",
author = "Cheng-Cheng Zhang and Hui-Yuan Wang and Min Zha and Cheng Wang and Jie-Hua Li and Zhi-Zheng Yang and Qi-Chuan Jiang",
year = "2018",
month = may,
day = "26",
doi = "10.3390/ma11060895",
language = "English",
volume = "11.2018",
journal = "Materials",
issn = "1996-1944",
publisher = "Multidisciplinary Digital Publishing Institute (MDPI)",
number = "6",

}

RIS (suitable for import to EndNote) - Download

TY - JOUR

T1 - Microstructure and Tensile Properties of AZ61 Alloy Sheets Processed by High-Ratio Extrusion with Subsequent Direct Aging Treatment

AU - Zhang, Cheng-Cheng

AU - Wang, Hui-Yuan

AU - Zha, Min

AU - Wang, Cheng

AU - Li, Jie-Hua

AU - Yang, Zhi-Zheng

AU - Jiang, Qi-Chuan

PY - 2018/5/26

Y1 - 2018/5/26

N2 - A high extrusion ratio of 166:1 was applied to commercial AZ61 alloy in one step with an extrusion speed of 2.1 m·min−1. The effects of DA (direct aging) treatment on the microstructure and tensile properties of extruded alloy were investigated. The extruded alloy exhibits fine DRXed grains and the average grain size is ~11 μm. After DA treatment at 170 °C, the tensile strength and 0.2% offset yield strength is enhanced from 314 to 336 MPa and from 169 to 191 MPa respectively, sacrificing elongation from 26.5% to 23.3%. The grain size and texture distribution of extruded AZ61 scarcely evolve during the post aging treatment. However, the enhanced strength in peak-aged alloy is mainly caused by the high-density elliptical Mg17Al12 precipitates distributing uniformly along the grain boundaries or within the grains, by precipitation and dispersion hardening. Furthermore, the nano-sized precipitates effectively inhibit grains from coarsening by triggering pinning effects along the grain boundaries at elevated temperature. As a result, the peak-aged alloy exhibits a better superplasticity of 306.5% compared with that of 231.8% of extruded sample. This work provides a practical one-step method for mass-producing Mg alloy sheets with excellent tensile strength and ductility compared with those fabricated by conventional extrusion methods.

AB - A high extrusion ratio of 166:1 was applied to commercial AZ61 alloy in one step with an extrusion speed of 2.1 m·min−1. The effects of DA (direct aging) treatment on the microstructure and tensile properties of extruded alloy were investigated. The extruded alloy exhibits fine DRXed grains and the average grain size is ~11 μm. After DA treatment at 170 °C, the tensile strength and 0.2% offset yield strength is enhanced from 314 to 336 MPa and from 169 to 191 MPa respectively, sacrificing elongation from 26.5% to 23.3%. The grain size and texture distribution of extruded AZ61 scarcely evolve during the post aging treatment. However, the enhanced strength in peak-aged alloy is mainly caused by the high-density elliptical Mg17Al12 precipitates distributing uniformly along the grain boundaries or within the grains, by precipitation and dispersion hardening. Furthermore, the nano-sized precipitates effectively inhibit grains from coarsening by triggering pinning effects along the grain boundaries at elevated temperature. As a result, the peak-aged alloy exhibits a better superplasticity of 306.5% compared with that of 231.8% of extruded sample. This work provides a practical one-step method for mass-producing Mg alloy sheets with excellent tensile strength and ductility compared with those fabricated by conventional extrusion methods.

U2 - 10.3390/ma11060895

DO - 10.3390/ma11060895

M3 - Article

VL - 11.2018

JO - Materials

JF - Materials

SN - 1996-1944

IS - 6

M1 - 895

ER -