Influence of partitioning parameters on the mechanical stability of austenite in a Q&P steel: A comparative in-situ study
Publikationen: Beitrag in Fachzeitschrift › Artikel › Forschung › (peer-reviewed)
Standard
in: Materialia, Jahrgang 15.2021, Nr. March, 101033, 03.2021.
Publikationen: Beitrag in Fachzeitschrift › Artikel › Forschung › (peer-reviewed)
Harvard
APA
Vancouver
Author
Bibtex - Download
}
RIS (suitable for import to EndNote) - Download
TY - JOUR
T1 - Influence of partitioning parameters on the mechanical stability of austenite in a Q&P steel: A comparative in-situ study
AU - Ebner, Sandra
AU - Schnitzer, Ronald
AU - Maawad, Emad
AU - Suppan, Clemens
AU - Hofer, Christina
N1 - Publisher Copyright: © 2021
PY - 2021/3
Y1 - 2021/3
N2 - The transformation-induced plasticity (TRIP)-effect is an efficient way to increase the formability in high performance steels. Hence, an optimal stability of the retained austenite is crucial to benefit the most from this effect. In the present work, in-situ high energy X-ray diffraction was used to study the austenite to martensite transformation upon uniaxial tensile loading of a TRIP-assisted steel produced by the quenching and partitioning (Q&P) process. A detailed analysis of the diffraction patterns recorded during deformation allowed to study the austenite stability with respect to the applied partitioning conditions. The austenite stability was found to strongly depend on the applied heat treatment, and could be mainly attributed to the carbon content and to the tempering degree of the surrounding martensitic matrix. Partitioning at 260 °C resulted in a poor austenite stability, while the austenite was almost too stable after partitioning at 360 °C. The optimal combination of strength and ductility was found for partitioning at 400 °C. The micromechanical behavior was analyzed by the evolution of individual lattice strains and the change of full width at half maximum (FWHM). Yielding of austenite could be clearly identified by an increase of FWHM. Martensite showed an unexpected peak narrowing upon yielding. In the case of 2-step Q&P, austenite started to yield after martensite, while yielding occurred almost simultaneously in the case of 1-step Q&P.
AB - The transformation-induced plasticity (TRIP)-effect is an efficient way to increase the formability in high performance steels. Hence, an optimal stability of the retained austenite is crucial to benefit the most from this effect. In the present work, in-situ high energy X-ray diffraction was used to study the austenite to martensite transformation upon uniaxial tensile loading of a TRIP-assisted steel produced by the quenching and partitioning (Q&P) process. A detailed analysis of the diffraction patterns recorded during deformation allowed to study the austenite stability with respect to the applied partitioning conditions. The austenite stability was found to strongly depend on the applied heat treatment, and could be mainly attributed to the carbon content and to the tempering degree of the surrounding martensitic matrix. Partitioning at 260 °C resulted in a poor austenite stability, while the austenite was almost too stable after partitioning at 360 °C. The optimal combination of strength and ductility was found for partitioning at 400 °C. The micromechanical behavior was analyzed by the evolution of individual lattice strains and the change of full width at half maximum (FWHM). Yielding of austenite could be clearly identified by an increase of FWHM. Martensite showed an unexpected peak narrowing upon yielding. In the case of 2-step Q&P, austenite started to yield after martensite, while yielding occurred almost simultaneously in the case of 1-step Q&P.
UR - http://www.scopus.com/inward/record.url?scp=85101121859&partnerID=8YFLogxK
U2 - 10.1016/j.mtla.2021.101033
DO - 10.1016/j.mtla.2021.101033
M3 - Article
VL - 15.2021
JO - Materialia
JF - Materialia
SN - 2589-1529
IS - March
M1 - 101033
ER -