Influence of corrosion fatigue on the stress gradient effect of the aluminium alloy EN AW-6082 T6

Publikationen: Beitrag in FachzeitschriftArtikelForschung(peer-reviewed)

Standard

Influence of corrosion fatigue on the stress gradient effect of the aluminium alloy EN AW-6082 T6. / Schönowitz, Markus; Maier, Bernd; Grün, Florian.
in: International Journal of Fatigue, Jahrgang 184.2024, Nr. July, 108322, 09.04.2024.

Publikationen: Beitrag in FachzeitschriftArtikelForschung(peer-reviewed)

Bibtex - Download

@article{5d2c11a6cfe24aa0b65170fca0287f42,
title = "Influence of corrosion fatigue on the stress gradient effect of the aluminium alloy EN AW-6082 T6",
abstract = "This study investigates the influence of corrosion fatigue on the fatigue strength of the aluminium alloy EN AW-6082 T6 with regard to the stress gradient. The experimental design involves varying loading conditions and specimen geometries to facilitate testing under three distinct stress gradients: tension/compression (0 mm -1), rotary bending (0.2 mm -1), notched rotary bending (5.3 mm -1). Reference constant loading tests in air as well as continuously irrigated corrosion fatigue tests in a 5 wt% NaCl-solution are conducted with a constant stress ratio of R =−1. The results reveal a substantial reduction in fatigue strength due to corrosion fatigue across all three stress gradients. The slope of the S-N curves drops by a factor of at least two and no second slope of the S-N curves is found within the tested load cycle range (up to 10 7). The study demonstrates a significant increase in the support factor for tests conducted in the corrosive environment. This discrepancy becomes more pronounced towards higher stress gradients and lower load cycle numbers. The application of the support factor derived from tests in a non-corrosive atmosphere is shown to be conservative, emphasizing the significance of accounting for corrosion effects in assessing fatigue behaviour.",
author = "Markus Sch{\"o}nowitz and Bernd Maier and Florian Gr{\"u}n",
note = "Publisher Copyright: {\textcopyright} 2024",
year = "2024",
month = apr,
day = "9",
doi = "10.1016/j.ijfatigue.2024.108322",
language = "English",
volume = "184.2024",
journal = "International Journal of Fatigue",
issn = "0142-1123",
publisher = "Elsevier",
number = "July",

}

RIS (suitable for import to EndNote) - Download

TY - JOUR

T1 - Influence of corrosion fatigue on the stress gradient effect of the aluminium alloy EN AW-6082 T6

AU - Schönowitz, Markus

AU - Maier, Bernd

AU - Grün, Florian

N1 - Publisher Copyright: © 2024

PY - 2024/4/9

Y1 - 2024/4/9

N2 - This study investigates the influence of corrosion fatigue on the fatigue strength of the aluminium alloy EN AW-6082 T6 with regard to the stress gradient. The experimental design involves varying loading conditions and specimen geometries to facilitate testing under three distinct stress gradients: tension/compression (0 mm -1), rotary bending (0.2 mm -1), notched rotary bending (5.3 mm -1). Reference constant loading tests in air as well as continuously irrigated corrosion fatigue tests in a 5 wt% NaCl-solution are conducted with a constant stress ratio of R =−1. The results reveal a substantial reduction in fatigue strength due to corrosion fatigue across all three stress gradients. The slope of the S-N curves drops by a factor of at least two and no second slope of the S-N curves is found within the tested load cycle range (up to 10 7). The study demonstrates a significant increase in the support factor for tests conducted in the corrosive environment. This discrepancy becomes more pronounced towards higher stress gradients and lower load cycle numbers. The application of the support factor derived from tests in a non-corrosive atmosphere is shown to be conservative, emphasizing the significance of accounting for corrosion effects in assessing fatigue behaviour.

AB - This study investigates the influence of corrosion fatigue on the fatigue strength of the aluminium alloy EN AW-6082 T6 with regard to the stress gradient. The experimental design involves varying loading conditions and specimen geometries to facilitate testing under three distinct stress gradients: tension/compression (0 mm -1), rotary bending (0.2 mm -1), notched rotary bending (5.3 mm -1). Reference constant loading tests in air as well as continuously irrigated corrosion fatigue tests in a 5 wt% NaCl-solution are conducted with a constant stress ratio of R =−1. The results reveal a substantial reduction in fatigue strength due to corrosion fatigue across all three stress gradients. The slope of the S-N curves drops by a factor of at least two and no second slope of the S-N curves is found within the tested load cycle range (up to 10 7). The study demonstrates a significant increase in the support factor for tests conducted in the corrosive environment. This discrepancy becomes more pronounced towards higher stress gradients and lower load cycle numbers. The application of the support factor derived from tests in a non-corrosive atmosphere is shown to be conservative, emphasizing the significance of accounting for corrosion effects in assessing fatigue behaviour.

UR - https://pureadmin.unileoben.ac.at/portal/en/publications/influence-of-corrosion-fatigue-on-the-stress-gradient-effect-of-the-aluminium-alloy-en-aw6082-t6(5d2c11a6-cfe2-4aa0-b651-70fca0287f42).html

UR - http://www.scopus.com/inward/record.url?scp=85189943692&partnerID=8YFLogxK

U2 - 10.1016/j.ijfatigue.2024.108322

DO - 10.1016/j.ijfatigue.2024.108322

M3 - Article

VL - 184.2024

JO - International Journal of Fatigue

JF - International Journal of Fatigue

SN - 0142-1123

IS - July

M1 - 108322

ER -