Influence of Binder Composition and Material Extrusion (MEX) Parameters on the 3D Printing of Highly Filled Copper Feedstocks

Publikationen: Beitrag in FachzeitschriftArtikelForschung(peer-reviewed)

Standard

Influence of Binder Composition and Material Extrusion (MEX) Parameters on the 3D Printing of Highly Filled Copper Feedstocks. / Sadaf, Mahrukh ; Cano Cano, Santiago; Gonzalez-Gutierrez, Joamin et al.
in: Polymers / Molecular Diversity Preservation International, Jahrgang 14.2022, Nr. 22, 4962, 16.11.2022.

Publikationen: Beitrag in FachzeitschriftArtikelForschung(peer-reviewed)

Bibtex - Download

@article{1a9799e868f74159887b73754624eb00,
title = "Influence of Binder Composition and Material Extrusion (MEX) Parameters on the 3D Printing of Highly Filled Copper Feedstocks",
abstract = "This work aims to better understand the type of thermoplastic binders required to produce highly loaded copper filaments that can be successfully printed via low-cost filament-based material extrusion (MEX). Compounding feedstock material with 55 vol.% of copper and three multi-component binder systems has been performed. The MEX behavior of these feedstocks was evaluated by depositing material at different speeds and appropriately selecting the extrusion temperature depending on the binder composition. The rest of the MEX parameters remained constant to evaluate the printing quality for the different feedstocks. Printable filaments were produced with low ovality and good surface quality. The filaments showed good dispersion of the powder and polymeric binder system in SEM analysis. The feedstock mechanical properties, i.e., the tensile strength of the filament, were sufficient to ensure proper feeding in the MEX machine. The viscosity of the feedstock systems at the adjusted printing temperatures lies in the range of 102–103 Pa·s at the shear rate of 100–1000 s−1, which appears to be sufficient to guarantee the correct flowability and continuous extrusion. The tensile properties vary greatly (e.g., ultimate tensile strength 3–9.8 MPa, elongation at break 1.5–40.5%), and the most fragile filament could not be reliably printed at higher speeds. Micrographs of the cross-section of printed parts revealed that as the printing speed increased, the porosity was minimized because the volumetric flow of the feedstock material increased, which can help to fill pores. This study offers new insights into the feedstock requirements needed to produce low-cost intricate copper components of high quality in a reliable and efficient manner. Such components can find many applications in the electronics, biomedical, and many other industries. ",
keywords = "additive manufacturing; copper; metals; material extrusion (MEX)",
author = "Mahrukh Sadaf and {Cano Cano}, Santiago and Joamin Gonzalez-Gutierrez and Mario Bragaglia and Stephan Schuschnigg and Christian Kukla and Clemens Holzer and Lilla V{\'a}ly and Michael Kitzmantel and Franesca Nanni",
year = "2022",
month = nov,
day = "16",
doi = "10.3390/polym14224962",
language = "English",
volume = "14.2022",
journal = "Polymers / Molecular Diversity Preservation International",
issn = "2073-4360",
publisher = "Multidisciplinary Digital Publishing Institute (MDPI)",
number = "22",

}

RIS (suitable for import to EndNote) - Download

TY - JOUR

T1 - Influence of Binder Composition and Material Extrusion (MEX) Parameters on the 3D Printing of Highly Filled Copper Feedstocks

AU - Sadaf, Mahrukh

AU - Cano Cano, Santiago

AU - Gonzalez-Gutierrez, Joamin

AU - Bragaglia, Mario

AU - Schuschnigg, Stephan

AU - Kukla, Christian

AU - Holzer, Clemens

AU - Vály , Lilla

AU - Kitzmantel, Michael

AU - Nanni, Franesca

PY - 2022/11/16

Y1 - 2022/11/16

N2 - This work aims to better understand the type of thermoplastic binders required to produce highly loaded copper filaments that can be successfully printed via low-cost filament-based material extrusion (MEX). Compounding feedstock material with 55 vol.% of copper and three multi-component binder systems has been performed. The MEX behavior of these feedstocks was evaluated by depositing material at different speeds and appropriately selecting the extrusion temperature depending on the binder composition. The rest of the MEX parameters remained constant to evaluate the printing quality for the different feedstocks. Printable filaments were produced with low ovality and good surface quality. The filaments showed good dispersion of the powder and polymeric binder system in SEM analysis. The feedstock mechanical properties, i.e., the tensile strength of the filament, were sufficient to ensure proper feeding in the MEX machine. The viscosity of the feedstock systems at the adjusted printing temperatures lies in the range of 102–103 Pa·s at the shear rate of 100–1000 s−1, which appears to be sufficient to guarantee the correct flowability and continuous extrusion. The tensile properties vary greatly (e.g., ultimate tensile strength 3–9.8 MPa, elongation at break 1.5–40.5%), and the most fragile filament could not be reliably printed at higher speeds. Micrographs of the cross-section of printed parts revealed that as the printing speed increased, the porosity was minimized because the volumetric flow of the feedstock material increased, which can help to fill pores. This study offers new insights into the feedstock requirements needed to produce low-cost intricate copper components of high quality in a reliable and efficient manner. Such components can find many applications in the electronics, biomedical, and many other industries.

AB - This work aims to better understand the type of thermoplastic binders required to produce highly loaded copper filaments that can be successfully printed via low-cost filament-based material extrusion (MEX). Compounding feedstock material with 55 vol.% of copper and three multi-component binder systems has been performed. The MEX behavior of these feedstocks was evaluated by depositing material at different speeds and appropriately selecting the extrusion temperature depending on the binder composition. The rest of the MEX parameters remained constant to evaluate the printing quality for the different feedstocks. Printable filaments were produced with low ovality and good surface quality. The filaments showed good dispersion of the powder and polymeric binder system in SEM analysis. The feedstock mechanical properties, i.e., the tensile strength of the filament, were sufficient to ensure proper feeding in the MEX machine. The viscosity of the feedstock systems at the adjusted printing temperatures lies in the range of 102–103 Pa·s at the shear rate of 100–1000 s−1, which appears to be sufficient to guarantee the correct flowability and continuous extrusion. The tensile properties vary greatly (e.g., ultimate tensile strength 3–9.8 MPa, elongation at break 1.5–40.5%), and the most fragile filament could not be reliably printed at higher speeds. Micrographs of the cross-section of printed parts revealed that as the printing speed increased, the porosity was minimized because the volumetric flow of the feedstock material increased, which can help to fill pores. This study offers new insights into the feedstock requirements needed to produce low-cost intricate copper components of high quality in a reliable and efficient manner. Such components can find many applications in the electronics, biomedical, and many other industries.

KW - additive manufacturing; copper; metals; material extrusion (MEX)

U2 - 10.3390/polym14224962

DO - 10.3390/polym14224962

M3 - Article

VL - 14.2022

JO - Polymers / Molecular Diversity Preservation International

JF - Polymers / Molecular Diversity Preservation International

SN - 2073-4360

IS - 22

M1 - 4962

ER -