Evaluation of the Influence Exerted by Increased Silicon Contents on the Leaching Behavior of NMC-Based Black Mass

Publikationen: Beitrag in FachzeitschriftArtikelForschung(peer-reviewed)

Standard

Evaluation of the Influence Exerted by Increased Silicon Contents on the Leaching Behavior of NMC-Based Black Mass. / Gerold, Eva; Lerchbammer, Reinhard; Antrekowitsch, Helmut.
in: Metals : open access journal , Jahrgang 13.2023, Nr. 4, 785, 17.04.2023.

Publikationen: Beitrag in FachzeitschriftArtikelForschung(peer-reviewed)

Bibtex - Download

@article{f90787ef3934429da1972c17ec695ff6,
title = "Evaluation of the Influence Exerted by Increased Silicon Contents on the Leaching Behavior of NMC-Based Black Mass",
abstract = "The further development of lithium-ion batteries leads to an improvement in power densities as well as safety and thus requires an optimization of the materials used. For this purpose, among other approaches, the anode materials are doped with silicon oxide or metallic silicon is used as the anode. However, silicon is a semimetal and is known to lead to the formation of jelly-like fluids in hydrometallurgical processes under certain conditions. This publication evaluates which parameters are responsible for this viscosity change in the leaching solutions during the recycling of lithium-ion batteries and examines the corresponding reaction mechanism behind this phenomenon. Furthermore, the leaching efficiency for the valuable metals nickel, cobalt, lithium and manganese is evaluated and the influence of different silicon contents in the solution is investigated. It could be shown that, especially the simultaneous presence of H2SO4, H2O2 and Si or SiO2, lead to a significant viscosity increase due to the formation of metasilicic acid and, accordingly, the leaching efficiencies of the valuable metals are negatively influenced.",
keywords = "Recyling, Lithium-Ionen-Batterien, neue Anodenmaterialien, Siliizium, Hydrometallurgie",
author = "Eva Gerold and Reinhard Lerchbammer and Helmut Antrekowitsch",
year = "2023",
month = apr,
day = "17",
doi = "10.3390/met13040785",
language = "English",
volume = "13.2023",
journal = "Metals : open access journal ",
issn = "2075-4701",
publisher = "Multidisciplinary Digital Publishing Institute (MDPI)",
number = "4",

}

RIS (suitable for import to EndNote) - Download

TY - JOUR

T1 - Evaluation of the Influence Exerted by Increased Silicon Contents on the Leaching Behavior of NMC-Based Black Mass

AU - Gerold, Eva

AU - Lerchbammer, Reinhard

AU - Antrekowitsch, Helmut

PY - 2023/4/17

Y1 - 2023/4/17

N2 - The further development of lithium-ion batteries leads to an improvement in power densities as well as safety and thus requires an optimization of the materials used. For this purpose, among other approaches, the anode materials are doped with silicon oxide or metallic silicon is used as the anode. However, silicon is a semimetal and is known to lead to the formation of jelly-like fluids in hydrometallurgical processes under certain conditions. This publication evaluates which parameters are responsible for this viscosity change in the leaching solutions during the recycling of lithium-ion batteries and examines the corresponding reaction mechanism behind this phenomenon. Furthermore, the leaching efficiency for the valuable metals nickel, cobalt, lithium and manganese is evaluated and the influence of different silicon contents in the solution is investigated. It could be shown that, especially the simultaneous presence of H2SO4, H2O2 and Si or SiO2, lead to a significant viscosity increase due to the formation of metasilicic acid and, accordingly, the leaching efficiencies of the valuable metals are negatively influenced.

AB - The further development of lithium-ion batteries leads to an improvement in power densities as well as safety and thus requires an optimization of the materials used. For this purpose, among other approaches, the anode materials are doped with silicon oxide or metallic silicon is used as the anode. However, silicon is a semimetal and is known to lead to the formation of jelly-like fluids in hydrometallurgical processes under certain conditions. This publication evaluates which parameters are responsible for this viscosity change in the leaching solutions during the recycling of lithium-ion batteries and examines the corresponding reaction mechanism behind this phenomenon. Furthermore, the leaching efficiency for the valuable metals nickel, cobalt, lithium and manganese is evaluated and the influence of different silicon contents in the solution is investigated. It could be shown that, especially the simultaneous presence of H2SO4, H2O2 and Si or SiO2, lead to a significant viscosity increase due to the formation of metasilicic acid and, accordingly, the leaching efficiencies of the valuable metals are negatively influenced.

KW - Recyling

KW - Lithium-Ionen-Batterien

KW - neue Anodenmaterialien

KW - Siliizium

KW - Hydrometallurgie

U2 - 10.3390/met13040785

DO - 10.3390/met13040785

M3 - Article

VL - 13.2023

JO - Metals : open access journal

JF - Metals : open access journal

SN - 2075-4701

IS - 4

M1 - 785

ER -