Controlling the high temperature deformation behavior and thermal stability of ultra-fine-grained W by re alloying
Publikationen: Beitrag in Fachzeitschrift › Artikel › Forschung › (peer-reviewed)
Standard
in: Journal of Materials Research, Jahrgang 2021, Nr. 12, 25.01.2021, S. 2408-2419.
Publikationen: Beitrag in Fachzeitschrift › Artikel › Forschung › (peer-reviewed)
Harvard
APA
Vancouver
Author
Bibtex - Download
}
RIS (suitable for import to EndNote) - Download
TY - JOUR
T1 - Controlling the high temperature deformation behavior and thermal stability of ultra-fine-grained W by re alloying
AU - Kappacher, Johann
AU - Renk, Oliver
AU - Kiener, Daniel
AU - Clemens, Helmut
AU - Maier-Kiener, Verena
N1 - Publisher Copyright: © 2021, The Author(s).
PY - 2021/1/25
Y1 - 2021/1/25
N2 - Due to their outstanding properties, ultra-fine-grained tungsten and its alloys are promising candidates to be used in harsh environments, hence it is crucial to understand their high temperature behavior and underlying deformation mechanisms. Therefore, advanced nanoindentation techniques were applied to ultra-fine-grained tungsten–rhenium alloys up to 1073 K. A continuous hardness decrease up to 0.2 Tm is rationalized by a still dominating effect of the Peierls stress. However, the absence of well-established effects of Rhenium alloying, resulting in a reduced temperature dependence of strength for coarse-grained microstructures, was interpreted as an indication for a diminishing role of kink-pair formation in ultra-fine-grained metals with sufficiently fine grain size. Despite slight grain growth in W, dislocation–grain boundary interaction was identified as the dominating deformation mechanism above 0.2 Tm. Interaction and accommodation of lattice dislocations with grain boundaries was affected by a reduced boundary diffusivity through alloying with Re.
AB - Due to their outstanding properties, ultra-fine-grained tungsten and its alloys are promising candidates to be used in harsh environments, hence it is crucial to understand their high temperature behavior and underlying deformation mechanisms. Therefore, advanced nanoindentation techniques were applied to ultra-fine-grained tungsten–rhenium alloys up to 1073 K. A continuous hardness decrease up to 0.2 Tm is rationalized by a still dominating effect of the Peierls stress. However, the absence of well-established effects of Rhenium alloying, resulting in a reduced temperature dependence of strength for coarse-grained microstructures, was interpreted as an indication for a diminishing role of kink-pair formation in ultra-fine-grained metals with sufficiently fine grain size. Despite slight grain growth in W, dislocation–grain boundary interaction was identified as the dominating deformation mechanism above 0.2 Tm. Interaction and accommodation of lattice dislocations with grain boundaries was affected by a reduced boundary diffusivity through alloying with Re.
U2 - 10.1557/s43578-020-00026-z
DO - 10.1557/s43578-020-00026-z
M3 - Article
VL - 2021
SP - 2408
EP - 2419
JO - Journal of Materials Research
JF - Journal of Materials Research
SN - 0884-2914
IS - 12
ER -