Surface sulphide formation on high-temperature corrosion resistant alloys in a H2S-HCl-CO2 mixed atmosphere
Research output: Contribution to journal › Article › Research › peer-review
Standard
In: Corrosion science, Vol. 181.2021, No. 1 April, 109241, 01.04.2021.
Research output: Contribution to journal › Article › Research › peer-review
Harvard
APA
Vancouver
Author
Bibtex - Download
}
RIS (suitable for import to EndNote) - Download
TY - JOUR
T1 - Surface sulphide formation on high-temperature corrosion resistant alloys in a H2S-HCl-CO2 mixed atmosphere
AU - Nimmervoll, Manuela
AU - Schmid, Alexander
AU - Mori, Gregor Karl
AU - Hönig, Stefan
AU - Haubner, Roland
N1 - Publisher Copyright: © 2021 Elsevier Ltd
PY - 2021/4/1
Y1 - 2021/4/1
N2 - In this paper the corrosion behavior of high temperature corrosion resistant alloys is investigated in a gas atmosphere containing HCl and H 2S at 480 °C and 680 °C. By considering the vapor pressures of the metal chlorides and the water gas shift reaction, as well as the influence of H 2S, the different corrosion behavior at 480 °C compared to 680 °C can be explained and a model of the course of corrosion is proposed. Corrosion tests were performed for 240 h with the austenitic stainless steels S31400 (20 wt% Ni) and N08811 (30.4 wt% Ni) and with the Ni-based alloy N06600 (72.5 wt% Ni). It could be shown that with increasing Ni-content in the alloy, the corrosion rate at high temperatures decreased, but this effect could no longer be observed at lower temperatures. While for N08811 and N06600 the mass loss was lower at 680 °C, it increased at temperatures of 480 °C. In the case of S31400 the mass loss increased with rising temperature.
AB - In this paper the corrosion behavior of high temperature corrosion resistant alloys is investigated in a gas atmosphere containing HCl and H 2S at 480 °C and 680 °C. By considering the vapor pressures of the metal chlorides and the water gas shift reaction, as well as the influence of H 2S, the different corrosion behavior at 480 °C compared to 680 °C can be explained and a model of the course of corrosion is proposed. Corrosion tests were performed for 240 h with the austenitic stainless steels S31400 (20 wt% Ni) and N08811 (30.4 wt% Ni) and with the Ni-based alloy N06600 (72.5 wt% Ni). It could be shown that with increasing Ni-content in the alloy, the corrosion rate at high temperatures decreased, but this effect could no longer be observed at lower temperatures. While for N08811 and N06600 the mass loss was lower at 680 °C, it increased at temperatures of 480 °C. In the case of S31400 the mass loss increased with rising temperature.
UR - http://www.scopus.com/inward/record.url?scp=85099358404&partnerID=8YFLogxK
U2 - 10.1016/j.corsci.2021.109241
DO - 10.1016/j.corsci.2021.109241
M3 - Article
VL - 181.2021
JO - Corrosion science
JF - Corrosion science
SN - 0010-938X
IS - 1 April
M1 - 109241
ER -