Phase equilibria in the Ti-rich part of the Ti-Al-Nb system: Part I: Low-Temperature Phase Equilibria Between 700 and 900 °C
Research output: Contribution to journal › Article › Research › peer-review
Authors
Organisational units
External Organisational units
- Max-Planck-Institut für Eisenforschung GmbH
- Institute of Coastal Research
Abstract
Precise knowledge of the phase equilibria in the Ti-Al-Nb system between 700 and 900 °C is of crucial importance for the urgently needed improvement of TiAl-based turbine materials already in industrial use to achieve further energy savings. As a result of the occurrence of the two ternary intermetallic phases ωo (“Ti4NbAl3”) and O (“Ti2NbAl”), which form in the solid state just in the range of the application-relevant temperatures, the phase relations are very complex and not well studied. In the present investigation, isothermal sections of the Ti-rich part of the Ti-Al-Nb system at 700, 800, and 900 °C were determined by a systematic study of 15 ternary alloys, one solid-solid diffusion couple, and three liquid-solid diffusion couples. Using scanning electron microscopy, electron probe microanalysis (EPMA), x-ray diffraction (XRD), high-energy XRD (HEXRD), differential thermal analysis (DTA), and transmission electron microscopy (TEM) investigations, type and composition of phases as well as phase transitions were determined. With these results, the phase equilibria were established. A focus of the investigations is on the homogeneity ranges of the two ternary phases ωo and O, which both are stable up to temperatures above 900 °C. Based on the compositions measured for the ωo phase and its crystal structure type, a new formula (Ti,Nb)2Al is suggested. The results also indicate that the phase field of the ωo phase is split into two parts at 900 °C because of the growing phase field of the ordered (βTi,Nb)o phase.
Details
Original language | English |
---|---|
Pages (from-to) | 355-381 |
Number of pages | 27 |
Journal | Journal of phase equilibria and diffusion |
Volume | 43.2022 |
Issue number | June |
DOIs | |
Publication status | Published - 1 Jul 2022 |