Adding 5 mass% wood pellets in a coal blend affects the reactivity with CO ₂ and microstructural properties of the coke at different final coking temperatures of 950 and 1100 °C. A correlation between coke reactivity index (CRI) and BET specific surface area was found. The reactivity of coke and biocoke decreases with a decrease in the specific surface area, as well as with an increase in the carbonization temperature. Raman spectroscopy results indicate that the higher carbonization temperature of biocoke mitigates the effect of 5 mass% of biomass addition. The X-ray diffraction-based interlayer spacing of carbon crystallite (d ₀₀₂) decreases slightly with increasing carbonization temperature, and crystallite height (L _c) increases with rising coking temperature for both coke and biocoke. Additionally, the lower the d ₀₀₂ value, the lower the CRI of the cokes and biocokes. A good correlation between CRI and d ₀₀₂ is observed. Carbon crystallite width (L _a) values increased with a rising carbonization temperature, indicating the intensive growth of carbon crystallites in all directions. However, these values for biocokes are lower due to the presence of charcoal particles.