How electron beam melting tailors the Al-sensitive microstructure and mechanical response of a novel process-adapted y-TiAl based alloy
Research output: Contribution to journal › Article › Research › peer-review
Authors
Organisational units
External Organisational units
- Friedrich-Alexander-Universität Erlangen-Nürnberg
Abstract
Additive manufacturing of lightweight intermetallic γ-TiAl based alloys combines process-related freedom of design with material-specific excellent high-temperature properties. Nevertheless, where locally melting the powder by an electron beam, there is a risk that Al evaporates due to its high vapor pressure, causing compositional and microstructural variations. This work investigates the impact of different process parameters on the total and local Al-content as well as the resulting as-built and heat-treated microstructure in a complex multiphase Ti-44.8Al-4.1Nb-0.7W-1.1Zr-0.4Si-0.5C-0.1B (at.%) alloy. The examinations applied are complementary, employing electron microscopy, X-ray spectroscopy and diffraction experiments with synchrotron X-ray radiation, supported by numerical simulations. The mechanical anisotropy of the heat-treated microstructure was analyzed by micro-hardness measurements. The results demonstrate that the amount of γ-TiAl phase decreases with increasing energy input of the electron beam in the as-built and heat-treated microstructure owing to the total and local loss of Al. Besides, the investigations of the crystal orientations within the multiphase alloy reveal a preferred orientation of the γ phase at high energy inputs. This follows from the fact that the preferred γ orientation is inherited through directional solidification of the β phase. The obtained process-microstructure-property relationships show that tailor-made material properties of additively manufactured γ-TiAl components are achievable.
Details
Original language | English |
---|---|
Article number | 110187 |
Number of pages | 13 |
Journal | Materials and Design |
Volume | 212.2021 |
Issue number | 15 December |
Early online date | 20 Oct 2021 |
DOIs | |
Publication status | Published - 15 Dec 2021 |