High failure resistance layered ceramics using crack bifurcation and interface delamination as reinforcement mechanisms
Research output: Contribution to journal › Article › Research › peer-review
Standard
High failure resistance layered ceramics using crack bifurcation and interface delamination as reinforcement mechanisms. / Bermejo Moratinos, Raul; Danzer, Robert.
In: Engineering Fracture Mechanics, Vol. 77, 2010, p. 2126-2135.
In: Engineering Fracture Mechanics, Vol. 77, 2010, p. 2126-2135.
Research output: Contribution to journal › Article › Research › peer-review
Harvard
APA
Vancouver
Bermejo Moratinos R, Danzer R. High failure resistance layered ceramics using crack bifurcation and interface delamination as reinforcement mechanisms. Engineering Fracture Mechanics. 2010;77:2126-2135. doi: 10.1016/j.engfracmech.2010.02.020
Author
Bibtex - Download
@article{0b788ce7c3a34b64b30762e3b059f352,
title = "High failure resistance layered ceramics using crack bifurcation and interface delamination as reinforcement mechanisms",
author = "{Bermejo Moratinos}, Raul and Robert Danzer",
year = "2010",
doi = "10.1016/j.engfracmech.2010.02.020",
language = "English",
volume = "77",
pages = "2126--2135",
journal = "Engineering Fracture Mechanics",
issn = "0013-7944",
publisher = "Elsevier",
}
RIS (suitable for import to EndNote) - Download
TY - JOUR
T1 - High failure resistance layered ceramics using crack bifurcation and interface delamination as reinforcement mechanisms
AU - Bermejo Moratinos, Raul
AU - Danzer, Robert
PY - 2010
Y1 - 2010
U2 - 10.1016/j.engfracmech.2010.02.020
DO - 10.1016/j.engfracmech.2010.02.020
M3 - Article
VL - 77
SP - 2126
EP - 2135
JO - Engineering Fracture Mechanics
JF - Engineering Fracture Mechanics
SN - 0013-7944
ER -