Effect of a single overload on the cyclic R-curve behaviour of a γ-TiAl TNM alloy

Research output: Contribution to journalArticleResearchpeer-review

Standard

Effect of a single overload on the cyclic R-curve behaviour of a γ-TiAl TNM alloy. / Lintner, Arthur; Pippan, Reinhard; Schloffer, Martin et al.
In: International Journal of Fatigue, Vol. 163.2022, No. October, 107083, 10.2022.

Research output: Contribution to journalArticleResearchpeer-review

Vancouver

Lintner A, Pippan R, Schloffer M, Hohenwarter A. Effect of a single overload on the cyclic R-curve behaviour of a γ-TiAl TNM alloy. International Journal of Fatigue. 2022 Oct;163.2022(October):107083. Epub 2022 Jun 23. doi: 10.1016/j.ijfatigue.2022.107083

Bibtex - Download

@article{63216d3f56cc4861a9b3777e6810d80a,
title = "Effect of a single overload on the cyclic R-curve behaviour of a γ-TiAl TNM alloy",
abstract = "The effect of single overloads on the threshold of stress intensity range of a semi-brittle material, a γ-titanium aluminide, was analysed. This material class exhibits a pronounced R-curve behaviour, which is mainly caused by the formation of shear ligaments, crack deflection and branching. Samples with short cracks on deep sharp notches were subjected to overloads of 80 % of the fracture toughness. Contrary to ductile materials, the experiments revealed no significant increase in the long-crack threshold, however a pronounced increase in the slope of the R-curve for the threshold of stress intensity range.",
keywords = "Fatigue threshold, Overload, R-curve, Titanium aluminide",
author = "Arthur Lintner and Reinhard Pippan and Martin Schloffer and Anton Hohenwarter",
note = "Publisher Copyright: {\textcopyright} 2022 The Authors",
year = "2022",
month = oct,
doi = "10.1016/j.ijfatigue.2022.107083",
language = "English",
volume = "163.2022",
journal = "International Journal of Fatigue",
issn = "0142-1123",
publisher = "Elsevier",
number = "October",

}

RIS (suitable for import to EndNote) - Download

TY - JOUR

T1 - Effect of a single overload on the cyclic R-curve behaviour of a γ-TiAl TNM alloy

AU - Lintner, Arthur

AU - Pippan, Reinhard

AU - Schloffer, Martin

AU - Hohenwarter, Anton

N1 - Publisher Copyright: © 2022 The Authors

PY - 2022/10

Y1 - 2022/10

N2 - The effect of single overloads on the threshold of stress intensity range of a semi-brittle material, a γ-titanium aluminide, was analysed. This material class exhibits a pronounced R-curve behaviour, which is mainly caused by the formation of shear ligaments, crack deflection and branching. Samples with short cracks on deep sharp notches were subjected to overloads of 80 % of the fracture toughness. Contrary to ductile materials, the experiments revealed no significant increase in the long-crack threshold, however a pronounced increase in the slope of the R-curve for the threshold of stress intensity range.

AB - The effect of single overloads on the threshold of stress intensity range of a semi-brittle material, a γ-titanium aluminide, was analysed. This material class exhibits a pronounced R-curve behaviour, which is mainly caused by the formation of shear ligaments, crack deflection and branching. Samples with short cracks on deep sharp notches were subjected to overloads of 80 % of the fracture toughness. Contrary to ductile materials, the experiments revealed no significant increase in the long-crack threshold, however a pronounced increase in the slope of the R-curve for the threshold of stress intensity range.

KW - Fatigue threshold

KW - Overload

KW - R-curve

KW - Titanium aluminide

UR - http://www.scopus.com/inward/record.url?scp=85132729142&partnerID=8YFLogxK

U2 - 10.1016/j.ijfatigue.2022.107083

DO - 10.1016/j.ijfatigue.2022.107083

M3 - Article

AN - SCOPUS:85132729142

VL - 163.2022

JO - International Journal of Fatigue

JF - International Journal of Fatigue

SN - 0142-1123

IS - October

M1 - 107083

ER -