Bonding Performance of Surface-Treated Zirconia Cantilevered Resin-Bonded Fixed Dental Prostheses: In Vitro Evaluation and Finite Element Analysis

Research output: Contribution to journalArticleResearchpeer-review

Standard

Bonding Performance of Surface-Treated Zirconia Cantilevered Resin-Bonded Fixed Dental Prostheses: In Vitro Evaluation and Finite Element Analysis. / Malgaj, Tine; Papšík, Roman; Abram, Anže et al.
In: Materials, Vol. 16, No. 7, 2646, 27.03.2023.

Research output: Contribution to journalArticleResearchpeer-review

Bibtex - Download

@article{b207aefadf2e42bc9d511ca062ce28cd,
title = "Bonding Performance of Surface-Treated Zirconia Cantilevered Resin-Bonded Fixed Dental Prostheses: In Vitro Evaluation and Finite Element Analysis",
abstract = "Debonding of zirconia cantilevered resin-bonded fixed dental prostheses (RBFDPs) remains the main treatment complication, therefore, the present in vitro study aimed to evaluate the effect of different surface pretreatments on the bonding of zirconia RBFDPs. Eighty milled zirconia maxillary central incisors, with complementary zirconia cantilevered RBFDPs, were randomly subjected to four different surface pretreatments (n = 20): as-machined (AM); airborne-particle abraded (APA); coated with nanostructured alumina coating (NAC); incisor air-abraded and RBFDP coated (NAC_APA). After bonding, half of each group (n = 10) was stored in deionized water (150 days/37 °C), thermocycled (37,500 cycles, 5–55 °C), and cyclically loaded (50 N/1.2 × 106). Load-bearing capacity (LBC) was determined using a quasi-static test. Additionally, finite element analysis (FEA) and fractography were performed. t-test and one-way ANOVA were used for statistical-analysis. Before aging, the NAC group provided superior LBC to other groups (p < 0.05). After aging, the AM specimens debonded spontaneously, while other groups exhibited comparable LBC (p > 0.05). The FEA results correlated with the in vitro experiment and fractography, showing highly stressed areas in the bonding interface, cement layer, and in RBFDP{\textquoteright}s retainer wing and connector. The NAC RBFDPs exhibited comparable long-term bonding performance to APA and should be regarded as a zirconia pretreatment alternative to APA.",
keywords = "bonding, dental stress analysis, finite element analysis, materials testing, resin bonded fixed partial denture, resin cements, zirconium dioxide",
author = "Tine Malgaj and Roman Pap{\v s}{\'i}k and An{\v z}e Abram and Andra{\v z} Kocjan and Peter Jevnikar",
year = "2023",
month = mar,
day = "27",
doi = "10.3390/ma16072646",
language = "English",
volume = "16",
journal = "Materials",
issn = "1996-1944",
publisher = "Multidisciplinary Digital Publishing Institute (MDPI)",
number = "7",

}

RIS (suitable for import to EndNote) - Download

TY - JOUR

T1 - Bonding Performance of Surface-Treated Zirconia Cantilevered Resin-Bonded Fixed Dental Prostheses

T2 - In Vitro Evaluation and Finite Element Analysis

AU - Malgaj, Tine

AU - Papšík, Roman

AU - Abram, Anže

AU - Kocjan, Andraž

AU - Jevnikar, Peter

PY - 2023/3/27

Y1 - 2023/3/27

N2 - Debonding of zirconia cantilevered resin-bonded fixed dental prostheses (RBFDPs) remains the main treatment complication, therefore, the present in vitro study aimed to evaluate the effect of different surface pretreatments on the bonding of zirconia RBFDPs. Eighty milled zirconia maxillary central incisors, with complementary zirconia cantilevered RBFDPs, were randomly subjected to four different surface pretreatments (n = 20): as-machined (AM); airborne-particle abraded (APA); coated with nanostructured alumina coating (NAC); incisor air-abraded and RBFDP coated (NAC_APA). After bonding, half of each group (n = 10) was stored in deionized water (150 days/37 °C), thermocycled (37,500 cycles, 5–55 °C), and cyclically loaded (50 N/1.2 × 106). Load-bearing capacity (LBC) was determined using a quasi-static test. Additionally, finite element analysis (FEA) and fractography were performed. t-test and one-way ANOVA were used for statistical-analysis. Before aging, the NAC group provided superior LBC to other groups (p < 0.05). After aging, the AM specimens debonded spontaneously, while other groups exhibited comparable LBC (p > 0.05). The FEA results correlated with the in vitro experiment and fractography, showing highly stressed areas in the bonding interface, cement layer, and in RBFDP’s retainer wing and connector. The NAC RBFDPs exhibited comparable long-term bonding performance to APA and should be regarded as a zirconia pretreatment alternative to APA.

AB - Debonding of zirconia cantilevered resin-bonded fixed dental prostheses (RBFDPs) remains the main treatment complication, therefore, the present in vitro study aimed to evaluate the effect of different surface pretreatments on the bonding of zirconia RBFDPs. Eighty milled zirconia maxillary central incisors, with complementary zirconia cantilevered RBFDPs, were randomly subjected to four different surface pretreatments (n = 20): as-machined (AM); airborne-particle abraded (APA); coated with nanostructured alumina coating (NAC); incisor air-abraded and RBFDP coated (NAC_APA). After bonding, half of each group (n = 10) was stored in deionized water (150 days/37 °C), thermocycled (37,500 cycles, 5–55 °C), and cyclically loaded (50 N/1.2 × 106). Load-bearing capacity (LBC) was determined using a quasi-static test. Additionally, finite element analysis (FEA) and fractography were performed. t-test and one-way ANOVA were used for statistical-analysis. Before aging, the NAC group provided superior LBC to other groups (p < 0.05). After aging, the AM specimens debonded spontaneously, while other groups exhibited comparable LBC (p > 0.05). The FEA results correlated with the in vitro experiment and fractography, showing highly stressed areas in the bonding interface, cement layer, and in RBFDP’s retainer wing and connector. The NAC RBFDPs exhibited comparable long-term bonding performance to APA and should be regarded as a zirconia pretreatment alternative to APA.

KW - bonding

KW - dental stress analysis

KW - finite element analysis

KW - materials testing

KW - resin bonded fixed partial denture

KW - resin cements

KW - zirconium dioxide

U2 - 10.3390/ma16072646

DO - 10.3390/ma16072646

M3 - Article

VL - 16

JO - Materials

JF - Materials

SN - 1996-1944

IS - 7

M1 - 2646

ER -