On the transition of failure control from material-intrinsic defects to defects forming during monotonically increasing and cyclic mechanical loading in WC-Co hard metal at elevated temperature

Publikationen: Beitrag in Fachzeitschrift › Artikel › Forschung › (peer-reviewed)

Standard

On the transition of failure control from material-intrinsic defects to defects forming during monotonically increasing and cyclic mechanical loading in WC-Co hard metal at elevated temperature. / Klünsner, Thomas; Lube, Tanja; Pichler, Peter et al.
in: Acta materialia, Jahrgang 235, 118087, 2022.

Publikationen: Beitrag in Fachzeitschrift › Artikel › Forschung › (peer-reviewed)

Harvard

Klünsner, T, Lube, T, Pichler, P, Krobath, M, Walch, L, Maier, K, Ecker, W, Marsoner, S, Czettl, C & Pippan, R 2022, 'On the transition of failure control from material-intrinsic defects to defects forming during monotonically increasing and cyclic mechanical loading in WC-Co hard metal at elevated temperature', Acta materialia, Jg. 235, 118087. https://doi.org/10.1016/j.actamat.2022.118087

APA

Klünsner, T., Lube, T., Pichler, P., Krobath, M., Walch, L., Maier, K., Ecker, W., Marsoner, S., Czettl, C., & Pippan, R. (2022). On the transition of failure control from material-intrinsic defects to defects forming during monotonically increasing and cyclic mechanical loading in WC-Co hard metal at elevated temperature. Acta materialia, 235, Artikel 118087. https://doi.org/10.1016/j.actamat.2022.118087

Vancouver

Klünsner T, Lube T, Pichler P, Krobath M, Walch L, Maier K et al. On the transition of failure control from material-intrinsic defects to defects forming during monotonically increasing and cyclic mechanical loading in WC-Co hard metal at elevated temperature. Acta materialia. 2022;235:118087. doi: https://doi.org/10.1016/j.actamat.2022.118087

Author

Klünsner, Thomas ; Lube, Tanja ; Pichler, Peter et al. / On the transition of failure control from material-intrinsic defects to defects forming during monotonically increasing and cyclic mechanical loading in WC-Co hard metal at elevated temperature. in: Acta materialia. 2022 ; Jahrgang 235.

Bibtex - Download

@article{533703def9cb4b639ab69d212e14f373,
title = "On the transition of failure control from material-intrinsic defects to defects forming during monotonically increasing and cyclic mechanical loading in WC-Co hard metal at elevated temperature",
author = "Thomas Kl{\"u}nsner and Tanja Lube and Peter Pichler and Martin Krobath and Lukas Walch and Kathrin Maier and Werner Ecker and Stefan Marsoner and Christoph Czettl and Reinhard Pippan",
year = "2022",
doi = "https://doi.org/10.1016/j.actamat.2022.118087",
language = "English",
volume = "235",
journal = "Acta materialia",
issn = "1359-6454",
publisher = "Elsevier",

}

RIS (suitable for import to EndNote) - Download

TY - JOUR

T1 - On the transition of failure control from material-intrinsic defects to defects forming during monotonically increasing and cyclic mechanical loading in WC-Co hard metal at elevated temperature

AU - Klünsner, Thomas

AU - Lube, Tanja

AU - Pichler, Peter

AU - Krobath, Martin

AU - Walch, Lukas

AU - Maier, Kathrin

AU - Ecker, Werner

AU - Marsoner, Stefan

AU - Czettl, Christoph

AU - Pippan, Reinhard

PY - 2022

Y1 - 2022

U2 - https://doi.org/10.1016/j.actamat.2022.118087

DO - https://doi.org/10.1016/j.actamat.2022.118087

M3 - Article

VL - 235

JO - Acta materialia

JF - Acta materialia

SN - 1359-6454

M1 - 118087

ER -

Beziehungsdiagramm anzeigen

360 Link

Zeitschriften in BUGL

Vom selben Autor

Mehr zeigen