Multiscale microstructures, mechanical properties and electrical conductivity of in-situ dual-size TiB2 particles reinforced 6201 aluminum matrix composites

Publikationen: Beitrag in FachzeitschriftArtikelForschung(peer-reviewed)

Standard

Multiscale microstructures, mechanical properties and electrical conductivity of in-situ dual-size TiB2 particles reinforced 6201 aluminum matrix composites. / Zhao, Kai; Liu, Xiangting ; Fang, Yuan et al.
in: Journal of Materials Research and Technology, Jahrgang 23.2023, Nr. March-April, 07.03.2023, S. 5459-5473.

Publikationen: Beitrag in FachzeitschriftArtikelForschung(peer-reviewed)

Vancouver

Bibtex - Download

@article{e3e46c4069a64725906ff9becedab528,
title = "Multiscale microstructures, mechanical properties and electrical conductivity of in-situ dual-size TiB2 particles reinforced 6201 aluminum matrix composites",
abstract = "The design of high-performance overhead aluminum wires is challenging, due to the intrinsic trade-off of strength-ductility and strength-electrical conductivity (EC). The in-situ halide salt reactions were used to introduce dual-size TiB2 particles into 6201 alloy to obtain out-bound mechanical properties with slight sacrifice of EC. With this strategy, the ultimate tensile strength, elongation after fracture and EC of the 4 wt%TiB2/6201Al composite are 360.9 MPa, 8.27% and 53.5% IACS, respectively, and these properties of the reference 6201 alloy are 325.0 MPa, 7.8% and 56.06% IACS. In the as-cast state, the majority of sub-micron TiB2 particles are segregated at the grain boundaries (termed as GBPs), forming a network pattern. The network is stretched along the rolling direction (RD) during deformation, and the orientation of GBPs is also rearranged from chaotic to a position with c axis nearly normal to the RD. In addition, semi-coherent particle/matrix interface is formed, which play a crucial role in strengthening the matrix. To optimize the EC, neutralization by adding Al–3B master alloy was performed, thus successfully eliminating the detrimental Al3Ti phase and precipitating excessive solute Ti atoms. The results show that not only the EC, but also the strength and ductility maximize at a composition around B:Ti = 2.0.",
author = "Kai Zhao and Xiangting Liu and Yuan Fang and Enyu Guo and Huijun Kang and Zhigang Hao and Jiehua LI and Guohao Du and Lei Liu and Zongning Chen and Tongming Wang",
note = "Publisher Copyright: {\textcopyright} 2023 The Author(s)",
year = "2023",
month = mar,
day = "7",
doi = "10.1016/j.jmrt.2023.02.174",
language = "English",
volume = "23.2023",
pages = "5459--5473",
journal = "Journal of Materials Research and Technology",
issn = "2238-7854",
publisher = "Elsevier",
number = "March-April",

}

RIS (suitable for import to EndNote) - Download

TY - JOUR

T1 - Multiscale microstructures, mechanical properties and electrical conductivity of in-situ dual-size TiB2 particles reinforced 6201 aluminum matrix composites

AU - Zhao, Kai

AU - Liu, Xiangting

AU - Fang, Yuan

AU - Guo, Enyu

AU - Kang, Huijun

AU - Hao, Zhigang

AU - LI, Jiehua

AU - Du, Guohao

AU - Liu, Lei

AU - Chen, Zongning

AU - Wang, Tongming

N1 - Publisher Copyright: © 2023 The Author(s)

PY - 2023/3/7

Y1 - 2023/3/7

N2 - The design of high-performance overhead aluminum wires is challenging, due to the intrinsic trade-off of strength-ductility and strength-electrical conductivity (EC). The in-situ halide salt reactions were used to introduce dual-size TiB2 particles into 6201 alloy to obtain out-bound mechanical properties with slight sacrifice of EC. With this strategy, the ultimate tensile strength, elongation after fracture and EC of the 4 wt%TiB2/6201Al composite are 360.9 MPa, 8.27% and 53.5% IACS, respectively, and these properties of the reference 6201 alloy are 325.0 MPa, 7.8% and 56.06% IACS. In the as-cast state, the majority of sub-micron TiB2 particles are segregated at the grain boundaries (termed as GBPs), forming a network pattern. The network is stretched along the rolling direction (RD) during deformation, and the orientation of GBPs is also rearranged from chaotic to a position with c axis nearly normal to the RD. In addition, semi-coherent particle/matrix interface is formed, which play a crucial role in strengthening the matrix. To optimize the EC, neutralization by adding Al–3B master alloy was performed, thus successfully eliminating the detrimental Al3Ti phase and precipitating excessive solute Ti atoms. The results show that not only the EC, but also the strength and ductility maximize at a composition around B:Ti = 2.0.

AB - The design of high-performance overhead aluminum wires is challenging, due to the intrinsic trade-off of strength-ductility and strength-electrical conductivity (EC). The in-situ halide salt reactions were used to introduce dual-size TiB2 particles into 6201 alloy to obtain out-bound mechanical properties with slight sacrifice of EC. With this strategy, the ultimate tensile strength, elongation after fracture and EC of the 4 wt%TiB2/6201Al composite are 360.9 MPa, 8.27% and 53.5% IACS, respectively, and these properties of the reference 6201 alloy are 325.0 MPa, 7.8% and 56.06% IACS. In the as-cast state, the majority of sub-micron TiB2 particles are segregated at the grain boundaries (termed as GBPs), forming a network pattern. The network is stretched along the rolling direction (RD) during deformation, and the orientation of GBPs is also rearranged from chaotic to a position with c axis nearly normal to the RD. In addition, semi-coherent particle/matrix interface is formed, which play a crucial role in strengthening the matrix. To optimize the EC, neutralization by adding Al–3B master alloy was performed, thus successfully eliminating the detrimental Al3Ti phase and precipitating excessive solute Ti atoms. The results show that not only the EC, but also the strength and ductility maximize at a composition around B:Ti = 2.0.

UR - http://www.scopus.com/inward/record.url?scp=85149774680&partnerID=8YFLogxK

U2 - 10.1016/j.jmrt.2023.02.174

DO - 10.1016/j.jmrt.2023.02.174

M3 - Article

VL - 23.2023

SP - 5459

EP - 5473

JO - Journal of Materials Research and Technology

JF - Journal of Materials Research and Technology

SN - 2238-7854

IS - March-April

ER -